Preparation and Structural Observation of Co₂MnSi Heusler Alloys by Mechanical Alloying
A Co₂MnSi Heusler alloy has been prepared by mechanical alloying (MA) method successfully using a mixture of elemental Co50Mn25Si25 powders. A two-phase mixture of amorphous phase and remaining Mn were obtained after 5 hours of MA without any evidence for the formation of Co₂MnSi alloys. The saturation magnetization of MA powders decreased with MA time due to the magnetic dilution by alloying with nonmagnetic Mn and Si elements to 48 emu/g after 5 hours of MA. On the other hand, a Co₂MnSi single phase was obtained by MA after 3 hours and subsequently heat treated up to 650 °C. X-ray diffraction result showed that the average grain size of Co₂MnSi Heusler alloys prepared by MA for 5 hours and heat treatment to be in the range of 85 nm. The saturation magnetization of Co₂MnSi Heusler alloys prepared by MA and heat treatment reached a maximum value of 112 emu/g for 5 hours MA sample. It was also observed that the coercivity of 5 hours MA sample annealed at 650 °C was fairly low value of 27 Oe.
Medienart: |
E-Artikel |
---|
Erscheinungsjahr: |
2020 |
---|---|
Erschienen: |
2020 |
Enthalten in: |
Zur Gesamtaufnahme - volume:20 |
---|---|
Enthalten in: |
Journal of nanoscience and nanotechnology - 20(2020), 9 vom: 01. Sept., Seite 5502-5505 |
Sprache: |
Englisch |
---|
Beteiligte Personen: |
Lee, Chung-Hyo [VerfasserIn] |
---|
Links: |
---|
Themen: |
---|
Anmerkungen: |
Date Revised 27.04.2020 published: Print Citation Status PubMed-not-MEDLINE |
---|
doi: |
10.1166/jnn.2020.17626 |
---|
funding: |
|
---|---|
Förderinstitution / Projekttitel: |
|
PPN (Katalog-ID): |
NLM309153522 |
---|
LEADER | 01000naa a22002652 4500 | ||
---|---|---|---|
001 | NLM309153522 | ||
003 | DE-627 | ||
005 | 20231225133302.0 | ||
007 | cr uuu---uuuuu | ||
008 | 231225s2020 xx |||||o 00| ||eng c | ||
024 | 7 | |a 10.1166/jnn.2020.17626 |2 doi | |
028 | 5 | 2 | |a pubmed24n1030.xml |
035 | |a (DE-627)NLM309153522 | ||
035 | |a (NLM)32331125 | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
100 | 1 | |a Lee, Chung-Hyo |e verfasserin |4 aut | |
245 | 1 | 0 | |a Preparation and Structural Observation of Co₂MnSi Heusler Alloys by Mechanical Alloying |
264 | 1 | |c 2020 | |
336 | |a Text |b txt |2 rdacontent | ||
337 | |a ƒaComputermedien |b c |2 rdamedia | ||
338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
500 | |a Date Revised 27.04.2020 | ||
500 | |a published: Print | ||
500 | |a Citation Status PubMed-not-MEDLINE | ||
520 | |a A Co₂MnSi Heusler alloy has been prepared by mechanical alloying (MA) method successfully using a mixture of elemental Co50Mn25Si25 powders. A two-phase mixture of amorphous phase and remaining Mn were obtained after 5 hours of MA without any evidence for the formation of Co₂MnSi alloys. The saturation magnetization of MA powders decreased with MA time due to the magnetic dilution by alloying with nonmagnetic Mn and Si elements to 48 emu/g after 5 hours of MA. On the other hand, a Co₂MnSi single phase was obtained by MA after 3 hours and subsequently heat treated up to 650 °C. X-ray diffraction result showed that the average grain size of Co₂MnSi Heusler alloys prepared by MA for 5 hours and heat treatment to be in the range of 85 nm. The saturation magnetization of Co₂MnSi Heusler alloys prepared by MA and heat treatment reached a maximum value of 112 emu/g for 5 hours MA sample. It was also observed that the coercivity of 5 hours MA sample annealed at 650 °C was fairly low value of 27 Oe | ||
650 | 4 | |a Journal Article | |
773 | 0 | 8 | |i Enthalten in |t Journal of nanoscience and nanotechnology |d 2001 |g 20(2020), 9 vom: 01. Sept., Seite 5502-5505 |w (DE-627)NLM126625220 |x 1533-4899 |7 nnns |
773 | 1 | 8 | |g volume:20 |g year:2020 |g number:9 |g day:01 |g month:09 |g pages:5502-5505 |
856 | 4 | 0 | |u http://dx.doi.org/10.1166/jnn.2020.17626 |3 Volltext |
912 | |a GBV_USEFLAG_A | ||
912 | |a GBV_NLM | ||
951 | |a AR | ||
952 | |d 20 |j 2020 |e 9 |b 01 |c 09 |h 5502-5505 |