Flash sintering of ultra‐high pure alumina ceramics with fine microstructure
Abstract The nearly fully dense ultra‐high pure (>99.99%) α‐Al2 O3 ceramics were prepared by flash sintering at the furnace temperature of 1300°C. Compared with the samples sintered at 1300 and 1650°C without electrical field, the flash‐sintered samples exhibited remarkably improved density and finer grains. The flash‐sintered samples also exhibited high hardness, which is even higher than that of the hot‐pressed sample. Therefore, it is believed that flash sintering could be an effective technique for the preparation of ultra‐high pure alumina ceramics..
Medienart: |
E-Artikel |
---|
Erscheinungsjahr: |
2022 |
---|---|
Erschienen: |
2022 |
Enthalten in: |
Zur Gesamtaufnahme - volume:105 |
---|---|
Enthalten in: |
Journal of the American Ceramic Society - 105(2022), 9, Seite 5569-5575 |
Beteiligte Personen: |
Yang, Shoulei [VerfasserIn] |
---|
BKL: |
---|
Anmerkungen: |
© 2022 The American Ceramic Society. |
---|
Umfang: |
7 |
---|
doi: |
10.1111/jace.18554 |
---|
funding: |
|
---|---|
Förderinstitution / Projekttitel: |
|
PPN (Katalog-ID): |
WLY007681496 |
---|
LEADER | 01000caa a22002652 4500 | ||
---|---|---|---|
001 | WLY007681496 | ||
003 | DE-627 | ||
005 | 20230307172235.0 | ||
007 | cr uuu---uuuuu | ||
008 | 230216s2022 xx |||||o 00| ||und c | ||
024 | 7 | |a 10.1111/jace.18554 |2 doi | |
028 | 5 | 2 | |a JACE_JACE18554.xml |
035 | |a (DE-627)WLY007681496 | ||
035 | |a (WILEY)JACE18554 | ||
040 | |a DE-627 |b ger |c DE-627 |e rda | ||
082 | 0 | 4 | |a 660 |q ASE |
084 | |a 51.60 |2 bkl | ||
084 | |a 58.45 |2 bkl | ||
100 | 1 | |a Yang, Shoulei |e verfasserin |4 aut | |
245 | 1 | 0 | |a Flash sintering of ultra‐high pure alumina ceramics with fine microstructure |
264 | 1 | |c 2022 | |
300 | |a 7 | ||
336 | |a Text |b txt |2 rdacontent | ||
337 | |a Computermedien |b c |2 rdamedia | ||
338 | |a Online-Ressource |b cr |2 rdacarrier | ||
500 | |a © 2022 The American Ceramic Society. | ||
520 | |a Abstract The nearly fully dense ultra‐high pure (>99.99%) α‐Al2 O3 ceramics were prepared by flash sintering at the furnace temperature of 1300°C. Compared with the samples sintered at 1300 and 1650°C without electrical field, the flash‐sintered samples exhibited remarkably improved density and finer grains. The flash‐sintered samples also exhibited high hardness, which is even higher than that of the hot‐pressed sample. Therefore, it is believed that flash sintering could be an effective technique for the preparation of ultra‐high pure alumina ceramics. | ||
700 | 1 | |a Zhu, Yinxiao |4 aut | |
700 | 1 | |a Yang, Sirui |4 aut | |
700 | 1 | |a Fu, Xinxin |4 aut | |
700 | 1 | |a Wei, Pengfei |4 aut | |
700 | 1 | |a Fan, Lei |4 aut | |
700 | 1 | |a Zhang, Mengwen |4 aut | |
700 | 1 | |a An, Linan |4 aut | |
773 | 0 | 8 | |i Enthalten in |t Journal of the American Ceramic Society |g 105(2022), 9, Seite 5569-5575 |w (DE-627)WLY007658753 |x 15512916 |7 nnns |
773 | 1 | 8 | |g volume:105 |g year:2022 |g number:9 |g pages:5569-5575 |g extent:7 |
912 | |a GBV_USEFLAG_A | ||
912 | |a GBV_WLY | ||
936 | b | k | |a 51.60 |q ASE |
936 | b | k | |a 58.45 |q ASE |
951 | |a AR | ||
952 | |d 105 |j 2022 |e 9 |h 5569-5575 |g 7 |