Effect of Tungsten Inert Gas Remelting on Microstructure and Corrosion Resistance of Q450NQR1 High-Strength Weathering Steel-Welded Joints
In this paper, the corrosion environment of a railway coal truck was simulated with 1.0%H2SO4 + 3%NaCl solution. The effect of weld toe Tungsten Inert Gas (TIG) remelting on the microstructure and corrosion resistance of welded joints of Q450NQR1 high-strength weathering steel was studied. The results show that the weld toe melts to form a remelting area after TIG remelting. After TIG remelting, the weld geometry was improved, and the stress concentration factor decreased from 1.17 to 1.06 at the weld toe, a decrease of 9.4%. TIG remelting refines the microstructure of the weld toe and improves the corrosion resistance of the welded joint. The surface of the TIG-remelted sample is uniformly corroded with no "deep and narrow" pits after the removal of corrosion products. The weight loss rate and corrosion rate of remelted welds are lower than those of unremelted welds. The structure of corrosion products is loose at the initial stage of corrosion, and the corrosion products are transformed into Fe3O4 and Fe2O3 protective rust layers with a dense structure after 480 h of corrosion. With the extension of corrosion time, the tensile strength and percentage elongation of the specimen decreased linearly. The decreasing rates of tensile strength of remelted and unremelted specimens were 0.09 and 0.11, respectively, and the decreasing rates of elongation after fracture were 0.0061 and 0.0076, respectively.
| Medienart: |
E-Artikel |
|---|
| Erscheinungsjahr: |
2024 |
|---|---|
| Erschienen: |
2024 |
| Enthalten in: |
Zur Gesamtaufnahme - volume:17 |
|---|---|
| Enthalten in: |
Materials (Basel, Switzerland) - 17(2024), 5 vom: 04. März |
| Sprache: |
Englisch |
|---|
| Beteiligte Personen: |
Li, Xuemei [VerfasserIn] |
|---|
| Links: |
|---|
| Themen: |
Corrosion resistance |
|---|
| Anmerkungen: |
Date Revised 15.03.2024 published: Electronic Citation Status PubMed-not-MEDLINE |
|---|
| doi: |
10.3390/ma17051198 |
|---|
| funding: |
|
|---|---|
| Förderinstitution / Projekttitel: |
|
| PPN (Katalog-ID): |
NLM369633822 |
|---|
| LEADER | 01000caa a22002652 4500 | ||
|---|---|---|---|
| 001 | NLM369633822 | ||
| 003 | DE-627 | ||
| 005 | 20240315233750.0 | ||
| 007 | cr uuu---uuuuu | ||
| 008 | 240313s2024 xx |||||o 00| ||eng c | ||
| 024 | 7 | |a 10.3390/ma17051198 |2 doi | |
| 028 | 5 | 2 | |a pubmed24n1330.xml |
| 035 | |a (DE-627)NLM369633822 | ||
| 035 | |a (NLM)38473669 | ||
| 035 | |a (PII)1198 | ||
| 040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
| 041 | |a eng | ||
| 100 | 1 | |a Li, Xuemei |e verfasserin |4 aut | |
| 245 | 1 | 0 | |a Effect of Tungsten Inert Gas Remelting on Microstructure and Corrosion Resistance of Q450NQR1 High-Strength Weathering Steel-Welded Joints |
| 264 | 1 | |c 2024 | |
| 336 | |a Text |b txt |2 rdacontent | ||
| 337 | |a ƒaComputermedien |b c |2 rdamedia | ||
| 338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
| 500 | |a Date Revised 15.03.2024 | ||
| 500 | |a published: Electronic | ||
| 500 | |a Citation Status PubMed-not-MEDLINE | ||
| 520 | |a In this paper, the corrosion environment of a railway coal truck was simulated with 1.0%H2SO4 + 3%NaCl solution. The effect of weld toe Tungsten Inert Gas (TIG) remelting on the microstructure and corrosion resistance of welded joints of Q450NQR1 high-strength weathering steel was studied. The results show that the weld toe melts to form a remelting area after TIG remelting. After TIG remelting, the weld geometry was improved, and the stress concentration factor decreased from 1.17 to 1.06 at the weld toe, a decrease of 9.4%. TIG remelting refines the microstructure of the weld toe and improves the corrosion resistance of the welded joint. The surface of the TIG-remelted sample is uniformly corroded with no "deep and narrow" pits after the removal of corrosion products. The weight loss rate and corrosion rate of remelted welds are lower than those of unremelted welds. The structure of corrosion products is loose at the initial stage of corrosion, and the corrosion products are transformed into Fe3O4 and Fe2O3 protective rust layers with a dense structure after 480 h of corrosion. With the extension of corrosion time, the tensile strength and percentage elongation of the specimen decreased linearly. The decreasing rates of tensile strength of remelted and unremelted specimens were 0.09 and 0.11, respectively, and the decreasing rates of elongation after fracture were 0.0061 and 0.0076, respectively | ||
| 650 | 4 | |a Journal Article | |
| 650 | 4 | |a TIG remelting | |
| 650 | 4 | |a corrosion resistance | |
| 650 | 4 | |a microstructure | |
| 650 | 4 | |a weathering steel | |
| 700 | 1 | |a Liu, Yang |e verfasserin |4 aut | |
| 700 | 1 | |a Guo, Rui |e verfasserin |4 aut | |
| 700 | 1 | |a Li, Zicheng |e verfasserin |4 aut | |
| 700 | 1 | |a Hu, Qingming |e verfasserin |4 aut | |
| 700 | 1 | |a Liu, Meng |e verfasserin |4 aut | |
| 700 | 1 | |a Zhu, Lei |e verfasserin |4 aut | |
| 700 | 1 | |a Kong, Xiangxia |e verfasserin |4 aut | |
| 773 | 0 | 8 | |i Enthalten in |t Materials (Basel, Switzerland) |d 2009 |g 17(2024), 5 vom: 04. März |w (DE-627)NLM208535349 |x 1996-1944 |7 nnns |
| 773 | 1 | 8 | |g volume:17 |g year:2024 |g number:5 |g day:04 |g month:03 |
| 856 | 4 | 0 | |u http://dx.doi.org/10.3390/ma17051198 |3 Volltext |
| 912 | |a GBV_USEFLAG_A | ||
| 912 | |a GBV_NLM | ||
| 951 | |a AR | ||
| 952 | |d 17 |j 2024 |e 5 |b 04 |c 03 | ||