Influence of post material and ferrule thickness on the fracture resistance of endodontically treated premolars : A laboratory study
Copyright © 2024 The Authors. Published by Elsevier Inc. All rights reserved..
STATEMENT OF PROBLEM: The influence of the ferrule thickness and post materials on the fracture resistance of endodontically treated teeth remains unclear.
PURPOSE: The purpose of this laboratory study was to evaluate the influence of post material and ferrule thickness on the fracture resistance of endodontically treated mandibular premolars.
MATERIAL AND METHODS: Sixty-four extracted and endodontically treated mandibular first premolars were used and divided into 4 test groups (n=16) depending on the ferrule thickness: F-0: without a ferrule, F-0.5: with a 0.5-mm ferrule thickness, F-1: with a 1-mm ferrule thickness, and F-1.5: with a 1.5-mm ferrule thickness. In groups with ferrules, the height ranged from 2 mm buccally/lingually to 1 mm proximally. Teeth in subgroups (n=8) were restored with either prefabricated glass fiber (FF) or titanium posts (FT) (ISO size 70 and length of 7.5 mm) and then adhesively restored with composite resin foundation materials. After foundation procedures, each specimen was restored with a cobalt chromium crown which was cemented with glass-ionomer cement. All specimens were subjected to dynamic loading in a masticatory simulator for 1 200 000 loading cycles with a nominal load of 5 Kg at 1.2 Hz and simultaneous thermocycling (5 to 55 °C). Specimens were then quasistatically loaded at 30 degrees in a universal testing machine until fracture. Fracture loads were analyzed by using 2-way ANOVA followed by the Tukey honestly significant difference test (α=.05).
RESULTS: Fracture loads ranged from 610 ±45 N (no ferrule - glass fiber post) to 1216 ±169 N (1.5 mm ferrule thickness - glass fiber post). A statistically significant increase in fracture resistance was observed with increasing ferrule thickness (P<.001). However, post materials did not show a statistically significant influence (P=.977).
CONCLUSIONS: Under the conditions of this laboratory study, increasing the ferrule thickness had a significant effect on the fracture resistance of endodontically treated teeth after thermomechanical fatigue, irrespective of post materials.
Medienart: |
E-Artikel |
---|
Erscheinungsjahr: |
2024 |
---|---|
Erschienen: |
2024 |
Enthalten in: |
Zur Gesamtaufnahme - year:2024 |
---|---|
Enthalten in: |
The Journal of prosthetic dentistry - (2024) vom: 23. Feb. |
Sprache: |
Englisch |
---|
Beteiligte Personen: |
Samran, Abdulaziz [VerfasserIn] |
---|
Links: |
---|
Themen: |
---|
Anmerkungen: |
Date Revised 24.02.2024 published: Print-Electronic Citation Status Publisher |
---|
doi: |
10.1016/j.prosdent.2024.01.022 |
---|
funding: |
|
---|---|
Förderinstitution / Projekttitel: |
|
PPN (Katalog-ID): |
NLM368921093 |
---|
LEADER | 01000naa a22002652 4500 | ||
---|---|---|---|
001 | NLM368921093 | ||
003 | DE-627 | ||
005 | 20240229152100.0 | ||
007 | cr uuu---uuuuu | ||
008 | 240229s2024 xx |||||o 00| ||eng c | ||
024 | 7 | |a 10.1016/j.prosdent.2024.01.022 |2 doi | |
028 | 5 | 2 | |a pubmed24n1305.xml |
035 | |a (DE-627)NLM368921093 | ||
035 | |a (NLM)38402134 | ||
035 | |a (PII)S0022-3913(24)00055-6 | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
100 | 1 | |a Samran, Abdulaziz |e verfasserin |4 aut | |
245 | 1 | 0 | |a Influence of post material and ferrule thickness on the fracture resistance of endodontically treated premolars |b A laboratory study |
264 | 1 | |c 2024 | |
336 | |a Text |b txt |2 rdacontent | ||
337 | |a ƒaComputermedien |b c |2 rdamedia | ||
338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
500 | |a Date Revised 24.02.2024 | ||
500 | |a published: Print-Electronic | ||
500 | |a Citation Status Publisher | ||
520 | |a Copyright © 2024 The Authors. Published by Elsevier Inc. All rights reserved. | ||
520 | |a STATEMENT OF PROBLEM: The influence of the ferrule thickness and post materials on the fracture resistance of endodontically treated teeth remains unclear | ||
520 | |a PURPOSE: The purpose of this laboratory study was to evaluate the influence of post material and ferrule thickness on the fracture resistance of endodontically treated mandibular premolars | ||
520 | |a MATERIAL AND METHODS: Sixty-four extracted and endodontically treated mandibular first premolars were used and divided into 4 test groups (n=16) depending on the ferrule thickness: F-0: without a ferrule, F-0.5: with a 0.5-mm ferrule thickness, F-1: with a 1-mm ferrule thickness, and F-1.5: with a 1.5-mm ferrule thickness. In groups with ferrules, the height ranged from 2 mm buccally/lingually to 1 mm proximally. Teeth in subgroups (n=8) were restored with either prefabricated glass fiber (FF) or titanium posts (FT) (ISO size 70 and length of 7.5 mm) and then adhesively restored with composite resin foundation materials. After foundation procedures, each specimen was restored with a cobalt chromium crown which was cemented with glass-ionomer cement. All specimens were subjected to dynamic loading in a masticatory simulator for 1 200 000 loading cycles with a nominal load of 5 Kg at 1.2 Hz and simultaneous thermocycling (5 to 55 °C). Specimens were then quasistatically loaded at 30 degrees in a universal testing machine until fracture. Fracture loads were analyzed by using 2-way ANOVA followed by the Tukey honestly significant difference test (α=.05) | ||
520 | |a RESULTS: Fracture loads ranged from 610 ±45 N (no ferrule - glass fiber post) to 1216 ±169 N (1.5 mm ferrule thickness - glass fiber post). A statistically significant increase in fracture resistance was observed with increasing ferrule thickness (P<.001). However, post materials did not show a statistically significant influence (P=.977) | ||
520 | |a CONCLUSIONS: Under the conditions of this laboratory study, increasing the ferrule thickness had a significant effect on the fracture resistance of endodontically treated teeth after thermomechanical fatigue, irrespective of post materials | ||
650 | 4 | |a Journal Article | |
700 | 1 | |a Hashem, Ahmed Wagdy |e verfasserin |4 aut | |
700 | 1 | |a Ali, Shurouk |e verfasserin |4 aut | |
700 | 1 | |a Al-Akhali, Majed |e verfasserin |4 aut | |
700 | 1 | |a Wille, Sebastian |e verfasserin |4 aut | |
700 | 1 | |a Kern, Matthias |e verfasserin |4 aut | |
773 | 0 | 8 | |i Enthalten in |t The Journal of prosthetic dentistry |d 1951 |g (2024) vom: 23. Feb. |w (DE-627)NLM000092541 |x 1097-6841 |7 nnns |
773 | 1 | 8 | |g year:2024 |g day:23 |g month:02 |
856 | 4 | 0 | |u http://dx.doi.org/10.1016/j.prosdent.2024.01.022 |3 Volltext |
912 | |a GBV_USEFLAG_A | ||
912 | |a GBV_NLM | ||
951 | |a AR | ||
952 | |j 2024 |b 23 |c 02 |