The Effect of Polyacrylate Emulsion Coating with Unmodified and Modified Nano-TiO2 on Weathering Resistance of Untreated and Heat-Treated Wood
In this research, the influence of titanium dioxide (TiO2) nanoparticles and their modifications on the weathering resistance of untreated and heat-treated wood was studied. The wood samples were coated with polyacrylate waterborne emulsion coatings that contain nano-TiO2 in the amount of 0.75 wt.%. Two types of modifiers were used to modify the nano-TiO2 surface: 2,2'-azobis(2-methylpropionamide) dihydrochloride (AIBA) and 3-aminopropyltrimethoxy silane (AMPTS). Coated and uncoated wood samples were exposed to accelerated weathering by application of sunlight, water and moisture for 360 h. During the research, the dry film thickness, color, gloss and hardness of the surface of the samples were measured. The obtained results showed that the effect of the addition and surface modification of nano-TiO2 on the color and gloss stability was different on untreated and heat-treated ash wood, and that accelerated weathering causes an increase in surface hardness and a decrease in thickness of the dry coating.
| Medienart: |
E-Artikel |
|---|
| Erscheinungsjahr: |
2024 |
|---|---|
| Erschienen: |
2024 |
| Enthalten in: |
Zur Gesamtaufnahme - volume:16 |
|---|---|
| Enthalten in: |
Polymers - 16(2024), 4 vom: 14. Feb. |
| Sprache: |
Englisch |
|---|
| Beteiligte Personen: |
Miklečić, Josip [VerfasserIn] |
|---|
| Links: |
|---|
| Themen: |
|---|
| Anmerkungen: |
Date Revised 27.02.2024 published: Electronic Citation Status PubMed-not-MEDLINE |
|---|
| doi: |
10.3390/polym16040511 |
|---|
| funding: |
|
|---|---|
| Förderinstitution / Projekttitel: |
|
| PPN (Katalog-ID): |
NLM368898687 |
|---|
| LEADER | 01000naa a22002652 4500 | ||
|---|---|---|---|
| 001 | NLM368898687 | ||
| 003 | DE-627 | ||
| 005 | 20240229164803.0 | ||
| 007 | cr uuu---uuuuu | ||
| 008 | 240229s2024 xx |||||o 00| ||eng c | ||
| 024 | 7 | |a 10.3390/polym16040511 |2 doi | |
| 028 | 5 | 2 | |a pubmed24n1309.xml |
| 035 | |a (DE-627)NLM368898687 | ||
| 035 | |a (NLM)38399889 | ||
| 035 | |a (PII)511 | ||
| 040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
| 041 | |a eng | ||
| 100 | 1 | |a Miklečić, Josip |e verfasserin |4 aut | |
| 245 | 1 | 4 | |a The Effect of Polyacrylate Emulsion Coating with Unmodified and Modified Nano-TiO2 on Weathering Resistance of Untreated and Heat-Treated Wood |
| 264 | 1 | |c 2024 | |
| 336 | |a Text |b txt |2 rdacontent | ||
| 337 | |a ƒaComputermedien |b c |2 rdamedia | ||
| 338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
| 500 | |a Date Revised 27.02.2024 | ||
| 500 | |a published: Electronic | ||
| 500 | |a Citation Status PubMed-not-MEDLINE | ||
| 520 | |a In this research, the influence of titanium dioxide (TiO2) nanoparticles and their modifications on the weathering resistance of untreated and heat-treated wood was studied. The wood samples were coated with polyacrylate waterborne emulsion coatings that contain nano-TiO2 in the amount of 0.75 wt.%. Two types of modifiers were used to modify the nano-TiO2 surface: 2,2'-azobis(2-methylpropionamide) dihydrochloride (AIBA) and 3-aminopropyltrimethoxy silane (AMPTS). Coated and uncoated wood samples were exposed to accelerated weathering by application of sunlight, water and moisture for 360 h. During the research, the dry film thickness, color, gloss and hardness of the surface of the samples were measured. The obtained results showed that the effect of the addition and surface modification of nano-TiO2 on the color and gloss stability was different on untreated and heat-treated ash wood, and that accelerated weathering causes an increase in surface hardness and a decrease in thickness of the dry coating | ||
| 650 | 4 | |a Journal Article | |
| 650 | 4 | |a coating | |
| 650 | 4 | |a heat-treated wood | |
| 650 | 4 | |a nano-TiO2 | |
| 650 | 4 | |a weathering | |
| 700 | 1 | |a Zeljko, Martina |e verfasserin |4 aut | |
| 700 | 1 | |a Lučić Blagojević, Sanja |e verfasserin |4 aut | |
| 700 | 1 | |a Jirouš-Rajković, Vlatka |e verfasserin |4 aut | |
| 773 | 0 | 8 | |i Enthalten in |t Polymers |d 2010 |g 16(2024), 4 vom: 14. Feb. |w (DE-627)NLM205507980 |x 2073-4360 |7 nnns |
| 773 | 1 | 8 | |g volume:16 |g year:2024 |g number:4 |g day:14 |g month:02 |
| 856 | 4 | 0 | |u http://dx.doi.org/10.3390/polym16040511 |3 Volltext |
| 912 | |a GBV_USEFLAG_A | ||
| 912 | |a GBV_NLM | ||
| 951 | |a AR | ||
| 952 | |d 16 |j 2024 |e 4 |b 14 |c 02 | ||