High-Entropy Oxide of (BiZrMoWCeLa)O2 as a Novel Catalyst for Vanadium Redox Flow Batteries
In this study, new fluorite high-entropy oxide (HEO), (BiZrMoWCeLa)O2, nanoparticles were produced using a surfactant-assisted hydrothermal technique followed by calcination and were used as novel catalytic materials for vanadium redox flow batteries (VRFBs). The HEO calcined at 750 °C (HEO-750) demonstrates superior electrocatalytic activity toward V3+/V2+ and VO2+/VO2+ redox couples compared to those of cells assembled with other samples. The charge-discharge tests further confirm that VRFBs using the HEO-750 catalyst demonstrate excellent Coulombic efficiency, voltage efficiency, and energy efficiency of 97.22, 87.47, and 85.04% at a current density of 80 mA cm-2 and 98.10, 74.76, and 73.34% at a higher current density of 160 mA cm-2, respectively. Moreover, with 500 charge-discharge cycles, there is no discernible degradation. These results are attributed to the calcination heat treatment, which induces the formation of a new single-phase fluorite structure, which facilitates the redox reactions of the vanadium redox couples. Furthermore, a high surface area, wettability, and plenty of oxygen vacancies can give more surface electroactive sites, improving the electrochemical performance, the charge transfer of the redox processes, and the stability of the VRFBs' electrode. This is the first report on the development of fluorite structure HEO nanoparticles in VRFBs, and it opens the door to further research into other HEOs.
| Medienart: |
E-Artikel |
|---|
| Erscheinungsjahr: |
2024 |
|---|---|
| Erschienen: |
2024 |
| Enthalten in: |
Zur Gesamtaufnahme - volume:16 |
|---|---|
| Enthalten in: |
ACS applied materials & interfaces - 16(2024), 8 vom: 28. Feb., Seite 10019-10032 |
| Sprache: |
Englisch |
|---|
| Beteiligte Personen: |
Demeku, Aknachew Mebreku [VerfasserIn] |
|---|
| Links: |
|---|
| Themen: |
Fluorite |
|---|
| Anmerkungen: |
Date Revised 06.03.2024 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
|---|
| doi: |
10.1021/acsami.3c15783 |
|---|
| funding: |
|
|---|---|
| Förderinstitution / Projekttitel: |
|
| PPN (Katalog-ID): |
NLM368647099 |
|---|
| LEADER | 01000caa a22002652 4500 | ||
|---|---|---|---|
| 001 | NLM368647099 | ||
| 003 | DE-627 | ||
| 005 | 20240306232939.0 | ||
| 007 | cr uuu---uuuuu | ||
| 008 | 240220s2024 xx |||||o 00| ||eng c | ||
| 024 | 7 | |a 10.1021/acsami.3c15783 |2 doi | |
| 028 | 5 | 2 | |a pubmed24n1318.xml |
| 035 | |a (DE-627)NLM368647099 | ||
| 035 | |a (NLM)38374647 | ||
| 040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
| 041 | |a eng | ||
| 100 | 1 | |a Demeku, Aknachew Mebreku |e verfasserin |4 aut | |
| 245 | 1 | 0 | |a High-Entropy Oxide of (BiZrMoWCeLa)O2 as a Novel Catalyst for Vanadium Redox Flow Batteries |
| 264 | 1 | |c 2024 | |
| 336 | |a Text |b txt |2 rdacontent | ||
| 337 | |a ƒaComputermedien |b c |2 rdamedia | ||
| 338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
| 500 | |a Date Revised 06.03.2024 | ||
| 500 | |a published: Print-Electronic | ||
| 500 | |a Citation Status PubMed-not-MEDLINE | ||
| 520 | |a In this study, new fluorite high-entropy oxide (HEO), (BiZrMoWCeLa)O2, nanoparticles were produced using a surfactant-assisted hydrothermal technique followed by calcination and were used as novel catalytic materials for vanadium redox flow batteries (VRFBs). The HEO calcined at 750 °C (HEO-750) demonstrates superior electrocatalytic activity toward V3+/V2+ and VO2+/VO2+ redox couples compared to those of cells assembled with other samples. The charge-discharge tests further confirm that VRFBs using the HEO-750 catalyst demonstrate excellent Coulombic efficiency, voltage efficiency, and energy efficiency of 97.22, 87.47, and 85.04% at a current density of 80 mA cm-2 and 98.10, 74.76, and 73.34% at a higher current density of 160 mA cm-2, respectively. Moreover, with 500 charge-discharge cycles, there is no discernible degradation. These results are attributed to the calcination heat treatment, which induces the formation of a new single-phase fluorite structure, which facilitates the redox reactions of the vanadium redox couples. Furthermore, a high surface area, wettability, and plenty of oxygen vacancies can give more surface electroactive sites, improving the electrochemical performance, the charge transfer of the redox processes, and the stability of the VRFBs' electrode. This is the first report on the development of fluorite structure HEO nanoparticles in VRFBs, and it opens the door to further research into other HEOs | ||
| 650 | 4 | |a Journal Article | |
| 650 | 4 | |a fluorite | |
| 650 | 4 | |a graphite felt | |
| 650 | 4 | |a high-entropy oxides | |
| 650 | 4 | |a single phase | |
| 650 | 4 | |a vanadium redox flow battery | |
| 700 | 1 | |a Kabtamu, Daniel Manaye |e verfasserin |4 aut | |
| 700 | 1 | |a Chen, Guan-Cheng |e verfasserin |4 aut | |
| 700 | 1 | |a Ou, Yun-Ting |e verfasserin |4 aut | |
| 700 | 1 | |a Huang, Zih-Jhong |e verfasserin |4 aut | |
| 700 | 1 | |a Hsu, Ning-Yih |e verfasserin |4 aut | |
| 700 | 1 | |a Ku, Hung-Hsien |e verfasserin |4 aut | |
| 700 | 1 | |a Wang, Yao-Ming |e verfasserin |4 aut | |
| 700 | 1 | |a Wang, Chen-Hao |e verfasserin |4 aut | |
| 773 | 0 | 8 | |i Enthalten in |t ACS applied materials & interfaces |d 2009 |g 16(2024), 8 vom: 28. Feb., Seite 10019-10032 |w (DE-627)NLM194100049 |x 1944-8252 |7 nnns |
| 773 | 1 | 8 | |g volume:16 |g year:2024 |g number:8 |g day:28 |g month:02 |g pages:10019-10032 |
| 856 | 4 | 0 | |u http://dx.doi.org/10.1021/acsami.3c15783 |3 Volltext |
| 912 | |a GBV_USEFLAG_A | ||
| 912 | |a GBV_NLM | ||
| 951 | |a AR | ||
| 952 | |d 16 |j 2024 |e 8 |b 28 |c 02 |h 10019-10032 | ||