Interface design for all-solid-state lithium batteries
© 2023. The Author(s), under exclusive licence to Springer Nature Limited..
The operation of high-energy all-solid-state lithium-metal batteries at low stack pressure is challenging owing to the Li dendrite growth at the Li anodes and the high interfacial resistance at the cathodes1-4. Here we design a Mg16Bi84 interlayer at the Li/Li6PS5Cl interface to suppress the Li dendrite growth, and a F-rich interlayer on LiNi0.8Mn0.1Co0.1O2 (NMC811) cathodes to reduce the interfacial resistance. During Li plating-stripping cycles, Mg migrates from the Mg16Bi84 interlayer to the Li anode converting Mg16Bi84 into a multifunctional LiMgSx-Li3Bi-LiMg structure with the layers functioning as a solid electrolyte interphase, a porous Li3Bi sublayer and a solid binder (welding porous Li3Bi onto the Li anode), respectively. The Li3Bi sublayer with its high ionic/electronic conductivity ratio allows Li to deposit only on the Li anode surface and grow into the porous Li3Bi sublayer, which ameliorates pressure (stress) changes. The NMC811 with the F-rich interlayer converts into F-doped NMC811 cathodes owing to the electrochemical migration of the F anion into the NMC811 at a high potential of 4.3 V stabilizing the cathodes. The anode and cathode interlayer designs enable the NMC811/Li6PS5Cl/Li cell to achieve a capacity of 7.2 mAh cm-2 at 2.55 mA cm-2, and the LiNiO2/Li6PS5Cl/Li cell to achieve a capacity of 11.1 mAh cm-2 with a cell-level energy density of 310 Wh kg-1 at a low stack pressure of 2.5 MPa. The Mg16Bi84 anode interlayer and F-rich cathode interlayer provide a general solution for all-solid-state lithium-metal batteries to achieve high energy and fast charging capability at low stack pressure.
| Medienart: |
E-Artikel |
|---|
| Erscheinungsjahr: |
2023 |
|---|---|
| Erschienen: |
2023 |
| Enthalten in: |
Zur Gesamtaufnahme - volume:623 |
|---|---|
| Enthalten in: |
Nature - 623(2023), 7988 vom: 25. Nov., Seite 739-744 |
| Sprache: |
Englisch |
|---|
| Beteiligte Personen: |
Wan, Hongli [VerfasserIn] |
|---|
| Links: |
|---|
| Themen: |
|---|
| Anmerkungen: |
Date Completed 25.11.2023 Date Revised 27.11.2023 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
|---|
| doi: |
10.1038/s41586-023-06653-w |
|---|
| funding: |
|
|---|---|
| Förderinstitution / Projekttitel: |
|
| PPN (Katalog-ID): |
NLM363725733 |
|---|
| LEADER | 01000naa a22002652 4500 | ||
|---|---|---|---|
| 001 | NLM363725733 | ||
| 003 | DE-627 | ||
| 005 | 20231226093948.0 | ||
| 007 | cr uuu---uuuuu | ||
| 008 | 231226s2023 xx |||||o 00| ||eng c | ||
| 024 | 7 | |a 10.1038/s41586-023-06653-w |2 doi | |
| 028 | 5 | 2 | |a pubmed24n1212.xml |
| 035 | |a (DE-627)NLM363725733 | ||
| 035 | |a (NLM)37880366 | ||
| 040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
| 041 | |a eng | ||
| 100 | 1 | |a Wan, Hongli |e verfasserin |4 aut | |
| 245 | 1 | 0 | |a Interface design for all-solid-state lithium batteries |
| 264 | 1 | |c 2023 | |
| 336 | |a Text |b txt |2 rdacontent | ||
| 337 | |a ƒaComputermedien |b c |2 rdamedia | ||
| 338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
| 500 | |a Date Completed 25.11.2023 | ||
| 500 | |a Date Revised 27.11.2023 | ||
| 500 | |a published: Print-Electronic | ||
| 500 | |a Citation Status PubMed-not-MEDLINE | ||
| 520 | |a © 2023. The Author(s), under exclusive licence to Springer Nature Limited. | ||
| 520 | |a The operation of high-energy all-solid-state lithium-metal batteries at low stack pressure is challenging owing to the Li dendrite growth at the Li anodes and the high interfacial resistance at the cathodes1-4. Here we design a Mg16Bi84 interlayer at the Li/Li6PS5Cl interface to suppress the Li dendrite growth, and a F-rich interlayer on LiNi0.8Mn0.1Co0.1O2 (NMC811) cathodes to reduce the interfacial resistance. During Li plating-stripping cycles, Mg migrates from the Mg16Bi84 interlayer to the Li anode converting Mg16Bi84 into a multifunctional LiMgSx-Li3Bi-LiMg structure with the layers functioning as a solid electrolyte interphase, a porous Li3Bi sublayer and a solid binder (welding porous Li3Bi onto the Li anode), respectively. The Li3Bi sublayer with its high ionic/electronic conductivity ratio allows Li to deposit only on the Li anode surface and grow into the porous Li3Bi sublayer, which ameliorates pressure (stress) changes. The NMC811 with the F-rich interlayer converts into F-doped NMC811 cathodes owing to the electrochemical migration of the F anion into the NMC811 at a high potential of 4.3 V stabilizing the cathodes. The anode and cathode interlayer designs enable the NMC811/Li6PS5Cl/Li cell to achieve a capacity of 7.2 mAh cm-2 at 2.55 mA cm-2, and the LiNiO2/Li6PS5Cl/Li cell to achieve a capacity of 11.1 mAh cm-2 with a cell-level energy density of 310 Wh kg-1 at a low stack pressure of 2.5 MPa. The Mg16Bi84 anode interlayer and F-rich cathode interlayer provide a general solution for all-solid-state lithium-metal batteries to achieve high energy and fast charging capability at low stack pressure | ||
| 650 | 4 | |a Journal Article | |
| 700 | 1 | |a Wang, Zeyi |e verfasserin |4 aut | |
| 700 | 1 | |a Zhang, Weiran |e verfasserin |4 aut | |
| 700 | 1 | |a He, Xinzi |e verfasserin |4 aut | |
| 700 | 1 | |a Wang, Chunsheng |e verfasserin |4 aut | |
| 773 | 0 | 8 | |i Enthalten in |t Nature |d 1945 |g 623(2023), 7988 vom: 25. Nov., Seite 739-744 |w (DE-627)NLM000008257 |x 1476-4687 |7 nnns |
| 773 | 1 | 8 | |g volume:623 |g year:2023 |g number:7988 |g day:25 |g month:11 |g pages:739-744 |
| 856 | 4 | 0 | |u http://dx.doi.org/10.1038/s41586-023-06653-w |3 Volltext |
| 912 | |a GBV_USEFLAG_A | ||
| 912 | |a GBV_NLM | ||
| 951 | |a AR | ||
| 952 | |d 623 |j 2023 |e 7988 |b 25 |c 11 |h 739-744 | ||