Analysis of the bond strength between conventional, putty or resin-modified calcium silicate cement and bulk fill composites
© 2023 Australian Dental Association..
BACKGROUND: The aim of this study was to evaluate the shear bond strength of three different calcium silicate-based cements (CBCs) with two different bulk-fill composite resins (CRs).
METHODS: Plexiglas moulds with a diameter of 4 mm and a thickness of 2 mm were prepared (n = 60). The Biodentine, NeoPutty and MTA Cem LC samples were randomly divided into two subgroups containing 10 samples each. Surfaces of samples were air dried and Single Bond universal adhesive was applied. Cylindrical plastic capsules of 4 mm height and 2 mm inner diameter belonging to Filtek Bulk-fill and EverX Posterior CRs were centred on coating material and polymerized for 20 s. After shear bond strength (SBS) testing, all samples were examined by scanning electron microscopy (SEM) to identify failure patterns. Three samples, one from each group, were prepared to evaluate chemical composition of CBCs and examined with an energy dispersive X-ray spectroscopy for surface elemental analysis.
RESULTS: The values obtained from the tests were evaluated as statistically significant (P < 0.05). After SBS testing, the difference between all CBCs was statistically significant in both CRs.
CONCLUSION: According to the findings in this study, it was concluded that MTA Cem LC had highest SBS values in both CRs. © 2023 Australian Dental Association.
| Medienart: |
E-Artikel |
|---|
| Erscheinungsjahr: |
2023 |
|---|---|
| Erschienen: |
2023 |
| Enthalten in: |
Zur Gesamtaufnahme - volume:68 |
|---|---|
| Enthalten in: |
Australian dental journal - 68(2023), 4 vom: 06. Dez., Seite 265-272 |
| Sprache: |
Englisch |
|---|
| Beteiligte Personen: |
Ipek, I [VerfasserIn] |
|---|
| Links: |
|---|
| Themen: |
Bulk fill composite |
|---|
| Anmerkungen: |
Date Completed 15.12.2023 Date Revised 15.12.2023 published: Print-Electronic Citation Status MEDLINE |
|---|
| doi: |
10.1111/adj.12977 |
|---|
| funding: |
|
|---|---|
| Förderinstitution / Projekttitel: |
|
| PPN (Katalog-ID): |
NLM361629621 |
|---|
| LEADER | 01000caa a22002652 4500 | ||
|---|---|---|---|
| 001 | NLM361629621 | ||
| 003 | DE-627 | ||
| 005 | 20231227131534.0 | ||
| 007 | cr uuu---uuuuu | ||
| 008 | 231226s2023 xx |||||o 00| ||eng c | ||
| 024 | 7 | |a 10.1111/adj.12977 |2 doi | |
| 028 | 5 | 2 | |a pubmed24n1225.xml |
| 035 | |a (DE-627)NLM361629621 | ||
| 035 | |a (NLM)37665246 | ||
| 040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
| 041 | |a eng | ||
| 100 | 1 | |a Ipek, I |e verfasserin |4 aut | |
| 245 | 1 | 0 | |a Analysis of the bond strength between conventional, putty or resin-modified calcium silicate cement and bulk fill composites |
| 264 | 1 | |c 2023 | |
| 336 | |a Text |b txt |2 rdacontent | ||
| 337 | |a ƒaComputermedien |b c |2 rdamedia | ||
| 338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
| 500 | |a Date Completed 15.12.2023 | ||
| 500 | |a Date Revised 15.12.2023 | ||
| 500 | |a published: Print-Electronic | ||
| 500 | |a Citation Status MEDLINE | ||
| 520 | |a © 2023 Australian Dental Association. | ||
| 520 | |a BACKGROUND: The aim of this study was to evaluate the shear bond strength of three different calcium silicate-based cements (CBCs) with two different bulk-fill composite resins (CRs) | ||
| 520 | |a METHODS: Plexiglas moulds with a diameter of 4 mm and a thickness of 2 mm were prepared (n = 60). The Biodentine, NeoPutty and MTA Cem LC samples were randomly divided into two subgroups containing 10 samples each. Surfaces of samples were air dried and Single Bond universal adhesive was applied. Cylindrical plastic capsules of 4 mm height and 2 mm inner diameter belonging to Filtek Bulk-fill and EverX Posterior CRs were centred on coating material and polymerized for 20 s. After shear bond strength (SBS) testing, all samples were examined by scanning electron microscopy (SEM) to identify failure patterns. Three samples, one from each group, were prepared to evaluate chemical composition of CBCs and examined with an energy dispersive X-ray spectroscopy for surface elemental analysis | ||
| 520 | |a RESULTS: The values obtained from the tests were evaluated as statistically significant (P < 0.05). After SBS testing, the difference between all CBCs was statistically significant in both CRs | ||
| 520 | |a CONCLUSION: According to the findings in this study, it was concluded that MTA Cem LC had highest SBS values in both CRs. © 2023 Australian Dental Association | ||
| 650 | 4 | |a Journal Article | |
| 650 | 4 | |a Randomized Controlled Trial | |
| 650 | 4 | |a Bulk fill composite | |
| 650 | 4 | |a failure type | |
| 650 | 4 | |a sem | |
| 650 | 4 | |a shear bond strength | |
| 650 | 4 | |a tricalcium silicate | |
| 650 | 7 | |a calcium silicate |2 NLM | |
| 650 | 7 | |a S4255P4G5M |2 NLM | |
| 650 | 7 | |a Composite Resins |2 NLM | |
| 650 | 7 | |a Glass Ionomer Cements |2 NLM | |
| 650 | 7 | |a Resin Cements |2 NLM | |
| 700 | 1 | |a Karaağaç Eskibağlar, B |e verfasserin |4 aut | |
| 700 | 1 | |a Yildiz, Ş |e verfasserin |4 aut | |
| 700 | 1 | |a Ataş, O |e verfasserin |4 aut | |
| 700 | 1 | |a Ünal, M |e verfasserin |4 aut | |
| 773 | 0 | 8 | |i Enthalten in |t Australian dental journal |d 1948 |g 68(2023), 4 vom: 06. Dez., Seite 265-272 |w (DE-627)NLM000027081 |x 1834-7819 |7 nnns |
| 773 | 1 | 8 | |g volume:68 |g year:2023 |g number:4 |g day:06 |g month:12 |g pages:265-272 |
| 856 | 4 | 0 | |u http://dx.doi.org/10.1111/adj.12977 |3 Volltext |
| 912 | |a GBV_USEFLAG_A | ||
| 912 | |a GBV_NLM | ||
| 951 | |a AR | ||
| 952 | |d 68 |j 2023 |e 4 |b 06 |c 12 |h 265-272 | ||