Effect of B-Doping and Manifestation on TiO2-Supported IrO2 for Oxygen Evolution Reaction in Water Electrolysis
To commercialize hydrogen production by proton exchange membrane (PEM) electrolysis, the amount of rare and precious metal (iridium) required for anodic oxygen evolution reaction (OER) must be greatly reduced. In order to solve the problem, carrier loading is used to reduce the amount of iridium. Unlike the carrier modified by conventional metal element doping, this work doped the carrier with the nonmetallic element and then prepared IrO2/TiBxO2 composite catalyst using the Adams melting method. B-doped TiO2 supports with different doping amounts show the main phase rutile structure. Among them, the conductivity of B-doped carrier shows an increasing trend with the increase of doping amount, because boron can form holes and negative centers after doping, and more carriers improve the conductivity of the support. In addition, since element B is manifested from inside to outside on the support, B can affect the catalytic process. After the manifestation of element B, the carrier loaded with IrO2 exhibited superior electrocatalytic properties. The voltammetric charge per unit mass of 40IrO2/TiB0.3O2#2 (where #2 represents B after manifestation) reaches 1970 mC (cm2 mg)-1, the corresponding overpotential is 273 mV at a current density of 10 mA/cm-2, and the Tafel slope is 61.9 mV/dec Also, the charge transfer resistance is only 15 Ω. Finally, in the stability test, the composite catalyst is also better than pure IrO2 in the 20 000 s operation. Therefore, element B has an unexpectedly positive effect on the catalytic progress on the surface of the support after its manifestation.
| Medienart: |
E-Artikel |
|---|
| Erscheinungsjahr: |
2023 |
|---|---|
| Erschienen: |
2023 |
| Enthalten in: |
Zur Gesamtaufnahme - volume:39 |
|---|---|
| Enthalten in: |
Langmuir : the ACS journal of surfaces and colloids - 39(2023), 11 vom: 21. März, Seite 4005-4014 |
| Sprache: |
Englisch |
|---|
| Beteiligte Personen: |
Wang, Tao [VerfasserIn] |
|---|
| Links: |
|---|
| Themen: |
|---|
| Anmerkungen: |
Date Completed 21.03.2023 Date Revised 21.03.2023 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
|---|
| doi: |
10.1021/acs.langmuir.2c03345 |
|---|
| funding: |
|
|---|---|
| Förderinstitution / Projekttitel: |
|
| PPN (Katalog-ID): |
NLM353876003 |
|---|
| LEADER | 01000naa a22002652 4500 | ||
|---|---|---|---|
| 001 | NLM353876003 | ||
| 003 | DE-627 | ||
| 005 | 20231226061020.0 | ||
| 007 | cr uuu---uuuuu | ||
| 008 | 231226s2023 xx |||||o 00| ||eng c | ||
| 024 | 7 | |a 10.1021/acs.langmuir.2c03345 |2 doi | |
| 028 | 5 | 2 | |a pubmed24n1179.xml |
| 035 | |a (DE-627)NLM353876003 | ||
| 035 | |a (NLM)36881819 | ||
| 040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
| 041 | |a eng | ||
| 100 | 1 | |a Wang, Tao |e verfasserin |4 aut | |
| 245 | 1 | 0 | |a Effect of B-Doping and Manifestation on TiO2-Supported IrO2 for Oxygen Evolution Reaction in Water Electrolysis |
| 264 | 1 | |c 2023 | |
| 336 | |a Text |b txt |2 rdacontent | ||
| 337 | |a ƒaComputermedien |b c |2 rdamedia | ||
| 338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
| 500 | |a Date Completed 21.03.2023 | ||
| 500 | |a Date Revised 21.03.2023 | ||
| 500 | |a published: Print-Electronic | ||
| 500 | |a Citation Status PubMed-not-MEDLINE | ||
| 520 | |a To commercialize hydrogen production by proton exchange membrane (PEM) electrolysis, the amount of rare and precious metal (iridium) required for anodic oxygen evolution reaction (OER) must be greatly reduced. In order to solve the problem, carrier loading is used to reduce the amount of iridium. Unlike the carrier modified by conventional metal element doping, this work doped the carrier with the nonmetallic element and then prepared IrO2/TiBxO2 composite catalyst using the Adams melting method. B-doped TiO2 supports with different doping amounts show the main phase rutile structure. Among them, the conductivity of B-doped carrier shows an increasing trend with the increase of doping amount, because boron can form holes and negative centers after doping, and more carriers improve the conductivity of the support. In addition, since element B is manifested from inside to outside on the support, B can affect the catalytic process. After the manifestation of element B, the carrier loaded with IrO2 exhibited superior electrocatalytic properties. The voltammetric charge per unit mass of 40IrO2/TiB0.3O2#2 (where #2 represents B after manifestation) reaches 1970 mC (cm2 mg)-1, the corresponding overpotential is 273 mV at a current density of 10 mA/cm-2, and the Tafel slope is 61.9 mV/dec Also, the charge transfer resistance is only 15 Ω. Finally, in the stability test, the composite catalyst is also better than pure IrO2 in the 20 000 s operation. Therefore, element B has an unexpectedly positive effect on the catalytic progress on the surface of the support after its manifestation | ||
| 650 | 4 | |a Journal Article | |
| 700 | 1 | |a Zeng, Yuting |e verfasserin |4 aut | |
| 700 | 1 | |a Xu, Mingyue |e verfasserin |4 aut | |
| 700 | 1 | |a Zhang, Jian |e verfasserin |4 aut | |
| 700 | 1 | |a Wu, Shengye |e verfasserin |4 aut | |
| 700 | 1 | |a Mu, Shichun |e verfasserin |4 aut | |
| 700 | 1 | |a Yu, Jun |e verfasserin |4 aut | |
| 773 | 0 | 8 | |i Enthalten in |t Langmuir : the ACS journal of surfaces and colloids |d 1999 |g 39(2023), 11 vom: 21. März, Seite 4005-4014 |w (DE-627)NLM098181009 |x 1520-5827 |7 nnns |
| 773 | 1 | 8 | |g volume:39 |g year:2023 |g number:11 |g day:21 |g month:03 |g pages:4005-4014 |
| 856 | 4 | 0 | |u http://dx.doi.org/10.1021/acs.langmuir.2c03345 |3 Volltext |
| 912 | |a GBV_USEFLAG_A | ||
| 912 | |a GBV_NLM | ||
| 951 | |a AR | ||
| 952 | |d 39 |j 2023 |e 11 |b 21 |c 03 |h 4005-4014 | ||