Facile Synthesis of Island-like ZrO2-VO2 Composite Films with Enhanced Thermochromic Performance for Smart Windows
VO2-based film, as a very promising thermochromic material for smart windows, has attracted extensive attention but has not been widely applied because it is difficult to simultaneously improve in terms of both solar-modulation efficiency (ΔTsol) and visible transmittance (Tlum) when made using the magnetron-sputtering method, and it has poor durability when made using the wet chemical method. Herein, island-like ZrO2-VO2 composite films with improved thermochromic performance (ΔTsol: 12.6%, Tlum: 45.0%) were created using a simple approach combining a dual magnetron-sputtering and acid-solution procedure. The film's ΔTsol and Tlum values were increased initially and subsequently declined as the sputtering power of the ZrO2 target was raised from 30 W to 120 W. ΔTsol achieved its maximum of 12.6% at 60 W, and Tlum reached its maximum of 51.1% at 90 W. This is likely the result of the interaction of two opposing effects: Some VO2 nanocrystals in the composite film were isolated by a few ZrO2 grains, and some pores could utilize their surface-plasmon-resonance effect at high temperature to absorb some near-infrared light for an enhanced ΔTsol and Tlum. More ZrO2 grains means fewer VO2 grains in the composite film and increased film thickness, which also results in a decrease in ΔTsol and Tlum. As a result, this work may offer a facile strategy to prepare VO2-based films with high thermochromic performance and promote their application in smart windows.
Medienart: |
E-Artikel |
---|
Erscheinungsjahr: |
2022 |
---|---|
Erschienen: |
2022 |
Enthalten in: |
Zur Gesamtaufnahme - volume:16 |
---|---|
Enthalten in: |
Materials (Basel, Switzerland) - 16(2022), 1 vom: 28. Dez. |
Sprache: |
Englisch |
---|
Beteiligte Personen: |
Wu, Jiahao [VerfasserIn] |
---|
Links: |
---|
Themen: |
Acid-solution process |
---|
Anmerkungen: |
Date Revised 11.01.2023 published: Electronic Citation Status PubMed-not-MEDLINE |
---|
doi: |
10.3390/ma16010273 |
---|
funding: |
|
---|---|
Förderinstitution / Projekttitel: |
|
PPN (Katalog-ID): |
NLM35125711X |
---|
LEADER | 01000naa a22002652 4500 | ||
---|---|---|---|
001 | NLM35125711X | ||
003 | DE-627 | ||
005 | 20231226050925.0 | ||
007 | cr uuu---uuuuu | ||
008 | 231226s2022 xx |||||o 00| ||eng c | ||
024 | 7 | |a 10.3390/ma16010273 |2 doi | |
028 | 5 | 2 | |a pubmed24n1170.xml |
035 | |a (DE-627)NLM35125711X | ||
035 | |a (NLM)36614618 | ||
035 | |a (PII)273 | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
100 | 1 | |a Wu, Jiahao |e verfasserin |4 aut | |
245 | 1 | 0 | |a Facile Synthesis of Island-like ZrO2-VO2 Composite Films with Enhanced Thermochromic Performance for Smart Windows |
264 | 1 | |c 2022 | |
336 | |a Text |b txt |2 rdacontent | ||
337 | |a ƒaComputermedien |b c |2 rdamedia | ||
338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
500 | |a Date Revised 11.01.2023 | ||
500 | |a published: Electronic | ||
500 | |a Citation Status PubMed-not-MEDLINE | ||
520 | |a VO2-based film, as a very promising thermochromic material for smart windows, has attracted extensive attention but has not been widely applied because it is difficult to simultaneously improve in terms of both solar-modulation efficiency (ΔTsol) and visible transmittance (Tlum) when made using the magnetron-sputtering method, and it has poor durability when made using the wet chemical method. Herein, island-like ZrO2-VO2 composite films with improved thermochromic performance (ΔTsol: 12.6%, Tlum: 45.0%) were created using a simple approach combining a dual magnetron-sputtering and acid-solution procedure. The film's ΔTsol and Tlum values were increased initially and subsequently declined as the sputtering power of the ZrO2 target was raised from 30 W to 120 W. ΔTsol achieved its maximum of 12.6% at 60 W, and Tlum reached its maximum of 51.1% at 90 W. This is likely the result of the interaction of two opposing effects: Some VO2 nanocrystals in the composite film were isolated by a few ZrO2 grains, and some pores could utilize their surface-plasmon-resonance effect at high temperature to absorb some near-infrared light for an enhanced ΔTsol and Tlum. More ZrO2 grains means fewer VO2 grains in the composite film and increased film thickness, which also results in a decrease in ΔTsol and Tlum. As a result, this work may offer a facile strategy to prepare VO2-based films with high thermochromic performance and promote their application in smart windows | ||
650 | 4 | |a Journal Article | |
650 | 4 | |a VO2-ZrO2 | |
650 | 4 | |a acid-solution process | |
650 | 4 | |a magnetron sputtering | |
650 | 4 | |a thermochromic properties | |
700 | 1 | |a Wang, Zhe |e verfasserin |4 aut | |
700 | 1 | |a Li, Bin |e verfasserin |4 aut | |
700 | 1 | |a Liu, Baoshun |e verfasserin |4 aut | |
700 | 1 | |a Zhao, Xiujian |e verfasserin |4 aut | |
700 | 1 | |a Tang, Gen |e verfasserin |4 aut | |
700 | 1 | |a Zeng, Dawen |e verfasserin |4 aut | |
700 | 1 | |a Tian, Shouqin |e verfasserin |4 aut | |
773 | 0 | 8 | |i Enthalten in |t Materials (Basel, Switzerland) |d 2009 |g 16(2022), 1 vom: 28. Dez. |w (DE-627)NLM208535349 |x 1996-1944 |7 nnns |
773 | 1 | 8 | |g volume:16 |g year:2022 |g number:1 |g day:28 |g month:12 |
856 | 4 | 0 | |u http://dx.doi.org/10.3390/ma16010273 |3 Volltext |
912 | |a GBV_USEFLAG_A | ||
912 | |a GBV_NLM | ||
951 | |a AR | ||
952 | |d 16 |j 2022 |e 1 |b 28 |c 12 |