Effect of Silane Coupling Agents on the Rheology, Dynamic and Mechanical Properties of Ethylene Propylene Diene Rubber/Calcium Carbonate Composites
The effects of three trimethoxysilanes with different functional groups on the rheology, dynamic and mechanical properties of ethylene propylene diene rubber (EPDM)/calcium carbonate (CaCO3) composites were investigated respectively. The results showed that the addition of silane increased the value of MH and MH-ML of the compounds. Geniosil XL 33 silane decreased the shear modulus of the EPDM/CaCO3 compounds, and the bound rubber content increased slightly with the addition of vinyl trimethoxy silane (VTMS) and methylacryloxy-methyltrimethoxysilane (Geniosil XL 33) silane in the compounds. The vulcanizates with the addition of the VTMS and Geniosil XL 33 silane showed a significant increase in tensile strength and abrasion resistance; however, ethyltrimethoxysilane (ETMS) silane weakened the tensile strength and abrasion resistance of the vulcanizates. At low strain, the cross-linking and reaggregation of fillers resulted in a high storage modulus of vulcanizates with silane. When the strain exceeded 10%, the storage modulus of the vulcanizates with the Geniosil XL 33 and VTMS silane was higher. The loss modulus and tan δ of the vulcanized rubber with the Geniosil XL 33 and VTMS silanes were lower compared to the ETMS and 0 silane.
Medienart: |
E-Artikel |
---|
Erscheinungsjahr: |
2022 |
---|---|
Erschienen: |
2022 |
Enthalten in: |
Zur Gesamtaufnahme - volume:14 |
---|---|
Enthalten in: |
Polymers - 14(2022), 16 vom: 19. Aug. |
Sprache: |
Englisch |
---|
Beteiligte Personen: |
Bi, Weina [VerfasserIn] |
---|
Links: |
---|
Themen: |
---|
Anmerkungen: |
Date Revised 30.08.2022 published: Electronic Citation Status PubMed-not-MEDLINE |
---|
doi: |
10.3390/polym14163393 |
---|
funding: |
|
---|---|
Förderinstitution / Projekttitel: |
|
PPN (Katalog-ID): |
NLM345340477 |
---|
LEADER | 01000naa a22002652 4500 | ||
---|---|---|---|
001 | NLM345340477 | ||
003 | DE-627 | ||
005 | 20231226024840.0 | ||
007 | cr uuu---uuuuu | ||
008 | 231226s2022 xx |||||o 00| ||eng c | ||
024 | 7 | |a 10.3390/polym14163393 |2 doi | |
028 | 5 | 2 | |a pubmed24n1151.xml |
035 | |a (DE-627)NLM345340477 | ||
035 | |a (NLM)36015653 | ||
035 | |a (PII)3393 | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
100 | 1 | |a Bi, Weina |e verfasserin |4 aut | |
245 | 1 | 0 | |a Effect of Silane Coupling Agents on the Rheology, Dynamic and Mechanical Properties of Ethylene Propylene Diene Rubber/Calcium Carbonate Composites |
264 | 1 | |c 2022 | |
336 | |a Text |b txt |2 rdacontent | ||
337 | |a ƒaComputermedien |b c |2 rdamedia | ||
338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
500 | |a Date Revised 30.08.2022 | ||
500 | |a published: Electronic | ||
500 | |a Citation Status PubMed-not-MEDLINE | ||
520 | |a The effects of three trimethoxysilanes with different functional groups on the rheology, dynamic and mechanical properties of ethylene propylene diene rubber (EPDM)/calcium carbonate (CaCO3) composites were investigated respectively. The results showed that the addition of silane increased the value of MH and MH-ML of the compounds. Geniosil XL 33 silane decreased the shear modulus of the EPDM/CaCO3 compounds, and the bound rubber content increased slightly with the addition of vinyl trimethoxy silane (VTMS) and methylacryloxy-methyltrimethoxysilane (Geniosil XL 33) silane in the compounds. The vulcanizates with the addition of the VTMS and Geniosil XL 33 silane showed a significant increase in tensile strength and abrasion resistance; however, ethyltrimethoxysilane (ETMS) silane weakened the tensile strength and abrasion resistance of the vulcanizates. At low strain, the cross-linking and reaggregation of fillers resulted in a high storage modulus of vulcanizates with silane. When the strain exceeded 10%, the storage modulus of the vulcanizates with the Geniosil XL 33 and VTMS silane was higher. The loss modulus and tan δ of the vulcanized rubber with the Geniosil XL 33 and VTMS silanes were lower compared to the ETMS and 0 silane | ||
650 | 4 | |a Journal Article | |
650 | 4 | |a cross-link | |
650 | 4 | |a interaction | |
650 | 4 | |a silane | |
700 | 1 | |a Goegelein, Christoph |e verfasserin |4 aut | |
700 | 1 | |a Hoch, Martin |e verfasserin |4 aut | |
700 | 1 | |a Kirchhoff, Joerg |e verfasserin |4 aut | |
700 | 1 | |a Zhao, Shugao |e verfasserin |4 aut | |
773 | 0 | 8 | |i Enthalten in |t Polymers |d 2010 |g 14(2022), 16 vom: 19. Aug. |w (DE-627)NLM205507980 |x 2073-4360 |7 nnns |
773 | 1 | 8 | |g volume:14 |g year:2022 |g number:16 |g day:19 |g month:08 |
856 | 4 | 0 | |u http://dx.doi.org/10.3390/polym14163393 |3 Volltext |
912 | |a GBV_USEFLAG_A | ||
912 | |a GBV_NLM | ||
951 | |a AR | ||
952 | |d 14 |j 2022 |e 16 |b 19 |c 08 |