Trivalent Chromium Ions Doped Fluorides with Both Broad Emission Bandwidth and Excellent Luminescence Thermal Stability
Recently, trivalent chromium ion doped phosphors have exhibited significant application potential in broadband near-infrared (NIR) phosphor-converted light-emitting diodes (pc-LEDs). However, developing an NIR phosphor with both broad emission bandwidth and excellent luminescence thermal stability is still a great challenge. Here, we demonstrate an NIR phosphor, ScF3:Cr3+, which can fulfill both conditions simultaneously. The prepared phosphors show broadband emission in the range of 700 to 1100 nm, with a full width at half-maximum (FWHM) of 140 nm peaking at 853 nm. These phosphors also demonstrate an excellent luminescence thermal stability (the emission intensity of ScF3:Cr3+ keeps 85.5% at 150 °C compared with the value at room temperature). An NIR pc-LED based on blue LED chips was fabricated and tested. The results show that the NIR pc-LED can yield strong broadband NIR emission. This work not only provides a promising phosphor for the application of NIR pc-LEDs but also has important guiding significance for effect of synthesis conditions on the luminescence properties of Cr3+-doped fluorides.
Medienart: |
E-Artikel |
---|
Erscheinungsjahr: |
2021 |
---|---|
Erschienen: |
2021 |
Enthalten in: |
Zur Gesamtaufnahme - volume:13 |
---|---|
Enthalten in: |
ACS applied materials & interfaces - 13(2021), 15 vom: 21. Apr., Seite 18274-18282 |
Sprache: |
Englisch |
---|
Beteiligte Personen: |
Lin, Qiuming [VerfasserIn] |
---|
Links: |
---|
Themen: |
Broadband |
---|
Anmerkungen: |
Date Revised 22.04.2021 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
---|
doi: |
10.1021/acsami.1c01417 |
---|
funding: |
|
---|---|
Förderinstitution / Projekttitel: |
|
PPN (Katalog-ID): |
NLM323859399 |
---|
LEADER | 01000naa a22002652 4500 | ||
---|---|---|---|
001 | NLM323859399 | ||
003 | DE-627 | ||
005 | 20231225185101.0 | ||
007 | cr uuu---uuuuu | ||
008 | 231225s2021 xx |||||o 00| ||eng c | ||
024 | 7 | |a 10.1021/acsami.1c01417 |2 doi | |
028 | 5 | 2 | |a pubmed24n1079.xml |
035 | |a (DE-627)NLM323859399 | ||
035 | |a (NLM)33830728 | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
100 | 1 | |a Lin, Qiuming |e verfasserin |4 aut | |
245 | 1 | 0 | |a Trivalent Chromium Ions Doped Fluorides with Both Broad Emission Bandwidth and Excellent Luminescence Thermal Stability |
264 | 1 | |c 2021 | |
336 | |a Text |b txt |2 rdacontent | ||
337 | |a ƒaComputermedien |b c |2 rdamedia | ||
338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
500 | |a Date Revised 22.04.2021 | ||
500 | |a published: Print-Electronic | ||
500 | |a Citation Status PubMed-not-MEDLINE | ||
520 | |a Recently, trivalent chromium ion doped phosphors have exhibited significant application potential in broadband near-infrared (NIR) phosphor-converted light-emitting diodes (pc-LEDs). However, developing an NIR phosphor with both broad emission bandwidth and excellent luminescence thermal stability is still a great challenge. Here, we demonstrate an NIR phosphor, ScF3:Cr3+, which can fulfill both conditions simultaneously. The prepared phosphors show broadband emission in the range of 700 to 1100 nm, with a full width at half-maximum (FWHM) of 140 nm peaking at 853 nm. These phosphors also demonstrate an excellent luminescence thermal stability (the emission intensity of ScF3:Cr3+ keeps 85.5% at 150 °C compared with the value at room temperature). An NIR pc-LED based on blue LED chips was fabricated and tested. The results show that the NIR pc-LED can yield strong broadband NIR emission. This work not only provides a promising phosphor for the application of NIR pc-LEDs but also has important guiding significance for effect of synthesis conditions on the luminescence properties of Cr3+-doped fluorides | ||
650 | 4 | |a Journal Article | |
650 | 4 | |a Cr3+ | |
650 | 4 | |a NIR pc-LEDs | |
650 | 4 | |a broadband | |
650 | 4 | |a fluorides | |
650 | 4 | |a luminescence thermal stability | |
700 | 1 | |a Wang, Qiang |e verfasserin |4 aut | |
700 | 1 | |a Liao, Min |e verfasserin |4 aut | |
700 | 1 | |a Xiong, Mingxiang |e verfasserin |4 aut | |
700 | 1 | |a Feng, Xing |e verfasserin |4 aut | |
700 | 1 | |a Zhang, Xin |e verfasserin |4 aut | |
700 | 1 | |a Dong, Huafeng |e verfasserin |4 aut | |
700 | 1 | |a Zhu, Daoyun |e verfasserin |4 aut | |
700 | 1 | |a Wu, Fugen |e verfasserin |4 aut | |
700 | 1 | |a Mu, Zhongfei |e verfasserin |4 aut | |
773 | 0 | 8 | |i Enthalten in |t ACS applied materials & interfaces |d 2009 |g 13(2021), 15 vom: 21. Apr., Seite 18274-18282 |w (DE-627)NLM194100049 |x 1944-8252 |7 nnns |
773 | 1 | 8 | |g volume:13 |g year:2021 |g number:15 |g day:21 |g month:04 |g pages:18274-18282 |
856 | 4 | 0 | |u http://dx.doi.org/10.1021/acsami.1c01417 |3 Volltext |
912 | |a GBV_USEFLAG_A | ||
912 | |a GBV_NLM | ||
951 | |a AR | ||
952 | |d 13 |j 2021 |e 15 |b 21 |c 04 |h 18274-18282 |