Thermal effect on the leachability of extraframework Co2+ in zeolite X
Copyright © 2020 Elsevier Ltd. All rights reserved..
A partially Co2+-exchanged zeolite X was thermally treated to simulate the effect of decay heat on the leachability of extraframework Co2+. To have a mechanistic insight into thermal effect, X-ray diffraction, scanning electron microscopy, 27Al magic angle spinning nuclear magnetic resonance spectroscopy, and Co K-edge X-ray absorption spectroscopy were employed with leaching tests. Although thermal treatment at ≤ 600 °C did not lead to the collapse of zeolite framework, it removed H2O molecules from the coordination shell of extraframework Co2+, which in turn changed its coordination structure in a way to strengthen the interaction between Co2+ and the lattice oxygens. In leaching tests, the sample treated at higher temperature for a longer period showed less remobilized Co2+ by forming a Co(OH)2-like surface precipitate and a Co hydrotalcite-like phase. Notably, the formation of the latter phase indicated the abstraction of the framework Al, the extent of which increased with the treatment temperature and duration. Two mechanisms, the concurrent extraction of Al with Co2+ remobilization and the hydrolysis-promoted Al abstraction, were proposed to account for thermally promoted dealumination. This study suggests that the exposure of Co2+-exchanged zeolite X to decay heat lessen the risk of extraframework Co2+ to be reintroduced into groundwater.
| Medienart: |
E-Artikel |
|---|
| Erscheinungsjahr: |
2021 |
|---|---|
| Erschienen: |
2021 |
| Enthalten in: |
Zur Gesamtaufnahme - volume:264 |
|---|---|
| Enthalten in: |
Chemosphere - 264(2021), Pt 1 vom: 15. Feb., Seite 128479 |
| Sprache: |
Englisch |
|---|
| Beteiligte Personen: |
Park, Minji [VerfasserIn] |
|---|
| Links: |
|---|
| Themen: |
1318-02-1 |
|---|
| Anmerkungen: |
Date Completed 22.12.2020 Date Revised 22.12.2020 published: Print-Electronic Citation Status MEDLINE |
|---|
| doi: |
10.1016/j.chemosphere.2020.128479 |
|---|
| funding: |
|
|---|---|
| Förderinstitution / Projekttitel: |
|
| PPN (Katalog-ID): |
NLM316022454 |
|---|
| LEADER | 01000naa a22002652 4500 | ||
|---|---|---|---|
| 001 | NLM316022454 | ||
| 003 | DE-627 | ||
| 005 | 20231225160158.0 | ||
| 007 | cr uuu---uuuuu | ||
| 008 | 231225s2021 xx |||||o 00| ||eng c | ||
| 024 | 7 | |a 10.1016/j.chemosphere.2020.128479 |2 doi | |
| 028 | 5 | 2 | |a pubmed24n1053.xml |
| 035 | |a (DE-627)NLM316022454 | ||
| 035 | |a (NLM)33032209 | ||
| 035 | |a (PII)S0045-6535(20)32674-6 | ||
| 040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
| 041 | |a eng | ||
| 100 | 1 | |a Park, Minji |e verfasserin |4 aut | |
| 245 | 1 | 0 | |a Thermal effect on the leachability of extraframework Co2+ in zeolite X |
| 264 | 1 | |c 2021 | |
| 336 | |a Text |b txt |2 rdacontent | ||
| 337 | |a ƒaComputermedien |b c |2 rdamedia | ||
| 338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
| 500 | |a Date Completed 22.12.2020 | ||
| 500 | |a Date Revised 22.12.2020 | ||
| 500 | |a published: Print-Electronic | ||
| 500 | |a Citation Status MEDLINE | ||
| 520 | |a Copyright © 2020 Elsevier Ltd. All rights reserved. | ||
| 520 | |a A partially Co2+-exchanged zeolite X was thermally treated to simulate the effect of decay heat on the leachability of extraframework Co2+. To have a mechanistic insight into thermal effect, X-ray diffraction, scanning electron microscopy, 27Al magic angle spinning nuclear magnetic resonance spectroscopy, and Co K-edge X-ray absorption spectroscopy were employed with leaching tests. Although thermal treatment at ≤ 600 °C did not lead to the collapse of zeolite framework, it removed H2O molecules from the coordination shell of extraframework Co2+, which in turn changed its coordination structure in a way to strengthen the interaction between Co2+ and the lattice oxygens. In leaching tests, the sample treated at higher temperature for a longer period showed less remobilized Co2+ by forming a Co(OH)2-like surface precipitate and a Co hydrotalcite-like phase. Notably, the formation of the latter phase indicated the abstraction of the framework Al, the extent of which increased with the treatment temperature and duration. Two mechanisms, the concurrent extraction of Al with Co2+ remobilization and the hydrolysis-promoted Al abstraction, were proposed to account for thermally promoted dealumination. This study suggests that the exposure of Co2+-exchanged zeolite X to decay heat lessen the risk of extraframework Co2+ to be reintroduced into groundwater | ||
| 650 | 4 | |a Journal Article | |
| 650 | 4 | |a Cobalt | |
| 650 | 4 | |a Dealumination | |
| 650 | 4 | |a Decay heat | |
| 650 | 4 | |a Hydrotalcite | |
| 650 | 4 | |a Zeolite | |
| 650 | 7 | |a Zeolites |2 NLM | |
| 650 | 7 | |a 1318-02-1 |2 NLM | |
| 700 | 1 | |a Kim, Sookyung |e verfasserin |4 aut | |
| 700 | 1 | |a Han, Young-Soo |e verfasserin |4 aut | |
| 700 | 1 | |a Hyun, Sung Pil |e verfasserin |4 aut | |
| 700 | 1 | |a Jeong, Hoon Young |e verfasserin |4 aut | |
| 773 | 0 | 8 | |i Enthalten in |t Chemosphere |d 1994 |g 264(2021), Pt 1 vom: 15. Feb., Seite 128479 |w (DE-627)NLM074698028 |x 1879-1298 |7 nnns |
| 773 | 1 | 8 | |g volume:264 |g year:2021 |g number:Pt 1 |g day:15 |g month:02 |g pages:128479 |
| 856 | 4 | 0 | |u http://dx.doi.org/10.1016/j.chemosphere.2020.128479 |3 Volltext |
| 912 | |a GBV_USEFLAG_A | ||
| 912 | |a GBV_NLM | ||
| 951 | |a AR | ||
| 952 | |d 264 |j 2021 |e Pt 1 |b 15 |c 02 |h 128479 | ||