Comparative Study on Chloride Binding Capacity of Cement-Fly Ash System and Cement-Ground Granulated Blast Furnace Slag System with Diethanol-Isopropanolamine
Steel bar corrosion caused by chloride was one of the main forms of concrete deterioration. The promotion of chloride binding capacity of cementitious materials would hinder the chloride transport to the surface of steel bar, thereby alleviating the corrosion and mitigating the deterioration. A comparative study on binding capacity of chloride in cement-fly ash system (C-FA) and cement-ground granulated blast furnace slag system (C-GGBS) with diethanol-isopropanolamine (DEIPA) was investigated in this study. Chloride ions was introduced by adding NaCl in paste, and the chloride binding capacity of the paste samples at 7 d and 60 d was examined. The hydration process was discussed via the testing of hydration heat and compressive strength. The hydrates in hardened paste was characterized by X-ray Diffractometry (XRD), Thermo Gravimetric Analysis (TGA), and Scanning Electron Microscope (SEM). The effect of DEIPA on dissolution of aluminate phase and compressive strength was discussed as well. These results showed that DEIPA could facilitate the hydration of C-FA and C-GGBS system, and the promotion effect was higher in C-FA than that in C-GGBS. DEIPA also increased the binding capacity of chloride in C-FA and C-GGBS systems. One reason was the increased chemical binding, because DEIPA facilitated the dissolution of aluminate to benefit the formation of Friedel's salt. Other reasons were the increased physical binding and migration resistance. By contrast, DEIPA presented greater ability to increase chloride binding capacity in C-FA system, because DEIPA showed stronger ability to expedite the dissolution of aluminate of FA than that of GGBS, which benefited the formation of FS, thereby promoting the chemical binding. Such results would give deep insight into using DEIPA as an additive in cement-based materials.
| Medienart: |
E-Artikel |
|---|
| Erscheinungsjahr: |
2020 |
|---|---|
| Erschienen: |
2020 |
| Enthalten in: |
Zur Gesamtaufnahme - volume:13 |
|---|---|
| Enthalten in: |
Materials (Basel, Switzerland) - 13(2020), 18 vom: 16. Sept. |
| Sprache: |
Englisch |
|---|
| Beteiligte Personen: |
Liu, Huaqing [VerfasserIn] |
|---|
| Links: |
|---|
| Themen: |
Chloride binding capacity |
|---|
| Anmerkungen: |
Date Revised 23.10.2020 published: Electronic Citation Status PubMed-not-MEDLINE |
|---|
| doi: |
10.3390/ma13184103 |
|---|
| funding: |
|
|---|---|
| Förderinstitution / Projekttitel: |
|
| PPN (Katalog-ID): |
NLM315192070 |
|---|
| LEADER | 01000naa a22002652 4500 | ||
|---|---|---|---|
| 001 | NLM315192070 | ||
| 003 | DE-627 | ||
| 005 | 20231225154357.0 | ||
| 007 | cr uuu---uuuuu | ||
| 008 | 231225s2020 xx |||||o 00| ||eng c | ||
| 024 | 7 | |a 10.3390/ma13184103 |2 doi | |
| 028 | 5 | 2 | |a pubmed24n1050.xml |
| 035 | |a (DE-627)NLM315192070 | ||
| 035 | |a (NLM)32947793 | ||
| 035 | |a (PII)E4103 | ||
| 040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
| 041 | |a eng | ||
| 100 | 1 | |a Liu, Huaqing |e verfasserin |4 aut | |
| 245 | 1 | 0 | |a Comparative Study on Chloride Binding Capacity of Cement-Fly Ash System and Cement-Ground Granulated Blast Furnace Slag System with Diethanol-Isopropanolamine |
| 264 | 1 | |c 2020 | |
| 336 | |a Text |b txt |2 rdacontent | ||
| 337 | |a ƒaComputermedien |b c |2 rdamedia | ||
| 338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
| 500 | |a Date Revised 23.10.2020 | ||
| 500 | |a published: Electronic | ||
| 500 | |a Citation Status PubMed-not-MEDLINE | ||
| 520 | |a Steel bar corrosion caused by chloride was one of the main forms of concrete deterioration. The promotion of chloride binding capacity of cementitious materials would hinder the chloride transport to the surface of steel bar, thereby alleviating the corrosion and mitigating the deterioration. A comparative study on binding capacity of chloride in cement-fly ash system (C-FA) and cement-ground granulated blast furnace slag system (C-GGBS) with diethanol-isopropanolamine (DEIPA) was investigated in this study. Chloride ions was introduced by adding NaCl in paste, and the chloride binding capacity of the paste samples at 7 d and 60 d was examined. The hydration process was discussed via the testing of hydration heat and compressive strength. The hydrates in hardened paste was characterized by X-ray Diffractometry (XRD), Thermo Gravimetric Analysis (TGA), and Scanning Electron Microscope (SEM). The effect of DEIPA on dissolution of aluminate phase and compressive strength was discussed as well. These results showed that DEIPA could facilitate the hydration of C-FA and C-GGBS system, and the promotion effect was higher in C-FA than that in C-GGBS. DEIPA also increased the binding capacity of chloride in C-FA and C-GGBS systems. One reason was the increased chemical binding, because DEIPA facilitated the dissolution of aluminate to benefit the formation of Friedel's salt. Other reasons were the increased physical binding and migration resistance. By contrast, DEIPA presented greater ability to increase chloride binding capacity in C-FA system, because DEIPA showed stronger ability to expedite the dissolution of aluminate of FA than that of GGBS, which benefited the formation of FS, thereby promoting the chemical binding. Such results would give deep insight into using DEIPA as an additive in cement-based materials | ||
| 650 | 4 | |a Journal Article | |
| 650 | 4 | |a chloride binding capacity | |
| 650 | 4 | |a diethanol-isopropanolamine | |
| 650 | 4 | |a fly ash | |
| 650 | 4 | |a ground granulated blast furnace slag | |
| 700 | 1 | |a Zhang, Yan |e verfasserin |4 aut | |
| 700 | 1 | |a Liu, Jialong |e verfasserin |4 aut | |
| 700 | 1 | |a Feng, Zixia |e verfasserin |4 aut | |
| 700 | 1 | |a Kong, Sen |e verfasserin |4 aut | |
| 773 | 0 | 8 | |i Enthalten in |t Materials (Basel, Switzerland) |d 2009 |g 13(2020), 18 vom: 16. Sept. |w (DE-627)NLM208535349 |x 1996-1944 |7 nnns |
| 773 | 1 | 8 | |g volume:13 |g year:2020 |g number:18 |g day:16 |g month:09 |
| 856 | 4 | 0 | |u http://dx.doi.org/10.3390/ma13184103 |3 Volltext |
| 912 | |a GBV_USEFLAG_A | ||
| 912 | |a GBV_NLM | ||
| 951 | |a AR | ||
| 952 | |d 13 |j 2020 |e 18 |b 16 |c 09 | ||