Strong electric wave response derived from the hybrid of lotus roots-like composites with tunable permittivity
Lotus roots-like NiO/NiCo2O4 hybrids derived from Metal-organic frameworks (MOFs) are fabricated for the first time by using flake NiCo-MOF precursors as reactant templates. It was found that a thin sample consisting of 60 wt % NiO/NiCo2O4 hybrids in the wax matrix exhibited an effective microwave absorption bandwidth of 4.2 GHz at the thickness of 1.6 mm. The highest reflection loss of -47 dB was observed at 13.4 GHz for a sample with a thickness of 1.7 mm. Results obtained in this study indicate that hybrids of NiO and NiCo2O4 are promising microwave absorbing materials with adjustable permittivity, which can exhibit broad effective absorption bandwidth at low filler loading and thin thickness.
Medienart: |
E-Artikel |
---|
Erscheinungsjahr: |
2017 |
---|---|
Erschienen: |
2017 |
Enthalten in: |
Zur Gesamtaufnahme - volume:7 |
---|---|
Enthalten in: |
Scientific reports - 7(2017), 1 vom: 25. Aug., Seite 9462 |
Sprache: |
Englisch |
---|
Beteiligte Personen: |
Liang, Xiaohui [VerfasserIn] |
---|
Links: |
---|
Themen: |
---|
Anmerkungen: |
Date Completed 14.03.2019 Date Revised 06.03.2020 published: Electronic Citation Status PubMed-not-MEDLINE |
---|
doi: |
10.1038/s41598-017-09985-6 |
---|
funding: |
|
---|---|
Förderinstitution / Projekttitel: |
|
PPN (Katalog-ID): |
NLM275153819 |
---|
LEADER | 01000caa a22002652 4500 | ||
---|---|---|---|
001 | NLM275153819 | ||
003 | DE-627 | ||
005 | 20231226194225.0 | ||
007 | cr uuu---uuuuu | ||
008 | 231225s2017 xx |||||o 00| ||eng c | ||
024 | 7 | |a 10.1038/s41598-017-09985-6 |2 doi | |
028 | 5 | 2 | |a pubmed24n0917.xml |
035 | |a (DE-627)NLM275153819 | ||
035 | |a (NLM)28842636 | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
100 | 1 | |a Liang, Xiaohui |e verfasserin |4 aut | |
245 | 1 | 0 | |a Strong electric wave response derived from the hybrid of lotus roots-like composites with tunable permittivity |
264 | 1 | |c 2017 | |
336 | |a Text |b txt |2 rdacontent | ||
337 | |a ƒaComputermedien |b c |2 rdamedia | ||
338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
500 | |a Date Completed 14.03.2019 | ||
500 | |a Date Revised 06.03.2020 | ||
500 | |a published: Electronic | ||
500 | |a Citation Status PubMed-not-MEDLINE | ||
520 | |a Lotus roots-like NiO/NiCo2O4 hybrids derived from Metal-organic frameworks (MOFs) are fabricated for the first time by using flake NiCo-MOF precursors as reactant templates. It was found that a thin sample consisting of 60 wt % NiO/NiCo2O4 hybrids in the wax matrix exhibited an effective microwave absorption bandwidth of 4.2 GHz at the thickness of 1.6 mm. The highest reflection loss of -47 dB was observed at 13.4 GHz for a sample with a thickness of 1.7 mm. Results obtained in this study indicate that hybrids of NiO and NiCo2O4 are promising microwave absorbing materials with adjustable permittivity, which can exhibit broad effective absorption bandwidth at low filler loading and thin thickness | ||
650 | 4 | |a Journal Article | |
650 | 4 | |a Research Support, Non-U.S. Gov't | |
700 | 1 | |a Quan, Bin |e verfasserin |4 aut | |
700 | 1 | |a Chen, Jiabin |e verfasserin |4 aut | |
700 | 1 | |a Tang, Dongming |e verfasserin |4 aut | |
700 | 1 | |a Zhang, Baoshan |e verfasserin |4 aut | |
700 | 1 | |a Ji, Guangbin |e verfasserin |4 aut | |
773 | 0 | 8 | |i Enthalten in |t Scientific reports |d 2011 |g 7(2017), 1 vom: 25. Aug., Seite 9462 |w (DE-627)NLM215703936 |x 2045-2322 |7 nnns |
773 | 1 | 8 | |g volume:7 |g year:2017 |g number:1 |g day:25 |g month:08 |g pages:9462 |
856 | 4 | 0 | |u http://dx.doi.org/10.1038/s41598-017-09985-6 |3 Volltext |
912 | |a GBV_USEFLAG_A | ||
912 | |a GBV_NLM | ||
951 | |a AR | ||
952 | |d 7 |j 2017 |e 1 |b 25 |c 08 |h 9462 |