Synthesis and characterization of the open-framework barium bisphosphonate [Ba3(O3PCH2NH2CH2PO3)2(H2O)4].3H2O
Following the strategy of using polyfunctional phosphonic acids for the synthesis of open-framework metal phosphonates, the phosphonocarboxylic acid (H2O3PCH2)2NCH2C6H4COOH was used in the hydrothermal synthesis of new Ba phosphonates. Its decomposition led to the first open-framework barium phosphonate [Ba3(O3PCH2NH2CH2PO3)2(H2O)4].3H2O. The synthesis was also successfully performed using iminobis(methylphosphonic acid), (H2O3PCH2)2NH, as a starting material, and the synthesis was optimized to obtain as a pure material. The reaction setup as well as the pH are the dominant parameters, and only a diffusion-controlled reaction led to the desired compound. The crystal structure was solved from single-crystal data: monoclinic; C2/c; a=2328.7(2), b=1359.95(7), and c=718.62(6) pm; beta=98.732(10) degrees ; V=2249.5(3)x10(6) pm3; Z=4; R1=0.036; and wR2=0.072 (all data). The structure of [Ba3(O3PCH2NH2CH2PO3)2(H2O)4].3H2O is built up from BaO8 and BaO10 polyhedra forming BaO chains and layers, respectively. These are connected to a three-dimensional metal-oxygen-metal framework with the iminobis(methylphosphonic acid) formally coating the inner walls of the pores. The one-dimensional pores (3.6x4 A) are filled with H2O molecules that can be thermally removed. Thermogravimetric investigations and temperature-dependent X-ray powder diffraction demonstrate the stability of the crystal structure up to 240 degrees C. The uptake of N,N-dimethylformamide and H2O by dehydrated samples is demonstrated. Furthermore, IR, Raman, and 31P magic-angle-spinning NMR data are also presented.
Medienart: |
Artikel |
---|
Erscheinungsjahr: |
2005 |
---|---|
Erschienen: |
2005 |
Enthalten in: |
Zur Gesamtaufnahme - volume:44 |
---|---|
Enthalten in: |
Inorganic chemistry - 44(2005), 25 vom: 12. Dez., Seite 9464-70 |
Sprache: |
Englisch |
---|
Beteiligte Personen: |
Bauer, Sebastian [VerfasserIn] |
---|
Themen: |
---|
Anmerkungen: |
Date Completed 19.07.2006 Date Revised 05.12.2005 published: Print Citation Status PubMed-not-MEDLINE |
---|
Förderinstitution / Projekttitel: |
|
---|
PPN (Katalog-ID): |
NLM159274745 |
---|
LEADER | 01000naa a22002652 4500 | ||
---|---|---|---|
001 | NLM159274745 | ||
003 | DE-627 | ||
005 | 20231223083819.0 | ||
007 | tu | ||
008 | 231223s2005 xx ||||| 00| ||eng c | ||
028 | 5 | 2 | |a pubmed24n0531.xml |
035 | |a (DE-627)NLM159274745 | ||
035 | |a (NLM)16323934 | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
100 | 1 | |a Bauer, Sebastian |e verfasserin |4 aut | |
245 | 1 | 0 | |a Synthesis and characterization of the open-framework barium bisphosphonate [Ba3(O3PCH2NH2CH2PO3)2(H2O)4].3H2O |
264 | 1 | |c 2005 | |
336 | |a Text |b txt |2 rdacontent | ||
337 | |a ohne Hilfsmittel zu benutzen |b n |2 rdamedia | ||
338 | |a Band |b nc |2 rdacarrier | ||
500 | |a Date Completed 19.07.2006 | ||
500 | |a Date Revised 05.12.2005 | ||
500 | |a published: Print | ||
500 | |a Citation Status PubMed-not-MEDLINE | ||
520 | |a Following the strategy of using polyfunctional phosphonic acids for the synthesis of open-framework metal phosphonates, the phosphonocarboxylic acid (H2O3PCH2)2NCH2C6H4COOH was used in the hydrothermal synthesis of new Ba phosphonates. Its decomposition led to the first open-framework barium phosphonate [Ba3(O3PCH2NH2CH2PO3)2(H2O)4].3H2O. The synthesis was also successfully performed using iminobis(methylphosphonic acid), (H2O3PCH2)2NH, as a starting material, and the synthesis was optimized to obtain as a pure material. The reaction setup as well as the pH are the dominant parameters, and only a diffusion-controlled reaction led to the desired compound. The crystal structure was solved from single-crystal data: monoclinic; C2/c; a=2328.7(2), b=1359.95(7), and c=718.62(6) pm; beta=98.732(10) degrees ; V=2249.5(3)x10(6) pm3; Z=4; R1=0.036; and wR2=0.072 (all data). The structure of [Ba3(O3PCH2NH2CH2PO3)2(H2O)4].3H2O is built up from BaO8 and BaO10 polyhedra forming BaO chains and layers, respectively. These are connected to a three-dimensional metal-oxygen-metal framework with the iminobis(methylphosphonic acid) formally coating the inner walls of the pores. The one-dimensional pores (3.6x4 A) are filled with H2O molecules that can be thermally removed. Thermogravimetric investigations and temperature-dependent X-ray powder diffraction demonstrate the stability of the crystal structure up to 240 degrees C. The uptake of N,N-dimethylformamide and H2O by dehydrated samples is demonstrated. Furthermore, IR, Raman, and 31P magic-angle-spinning NMR data are also presented | ||
650 | 4 | |a Journal Article | |
700 | 1 | |a Müller, Helen |e verfasserin |4 aut | |
700 | 1 | |a Bein, Thomas |e verfasserin |4 aut | |
700 | 1 | |a Stock, Norbert |e verfasserin |4 aut | |
773 | 0 | 8 | |i Enthalten in |t Inorganic chemistry |d 1966 |g 44(2005), 25 vom: 12. Dez., Seite 9464-70 |w (DE-627)NLM110650298 |x 1520-510X |7 nnns |
773 | 1 | 8 | |g volume:44 |g year:2005 |g number:25 |g day:12 |g month:12 |g pages:9464-70 |
912 | |a GBV_USEFLAG_A | ||
912 | |a GBV_NLM | ||
951 | |a AR | ||
952 | |d 44 |j 2005 |e 25 |b 12 |c 12 |h 9464-70 |