Synthesis and crystal growth of the high-Tc phase in Bi–Pb–Sr–Ca–Cu–O system with variation of excess concentrations of CaO and CuO
Analyzing the results measured by x-ray powder diffraction, scanning electron microscope, energy dispersion x-ray analysis, and the standard four-probe techniques for eight groups of samples with different compositions of excess CaO and CuO, after quenching and annealing, shows that not only the much more stable 2223 phase in the Bi(Pb)–Sr–Ca–Cu–O system was obtained in a high fraction, but also its grain (plate shaped) size could be made larger than normally sintered. We attribute these effects to the annealing and/or the excess contents of CaO and CuO selected in this study..
Medienart: |
E-Artikel |
---|
Erscheinungsjahr: |
1992 |
---|---|
Erschienen: |
1992 |
Reproduktion: |
AIP Digital Archive |
---|---|
Enthalten in: |
Zur Gesamtaufnahme - volume:71 |
Enthalten in: |
Journal of Applied Physics - 71(1992), 6, Seite 2772-2777 |
Sprache: |
Englisch |
---|
Beteiligte Personen: |
Wu, Qianzhang [Sonstige Person] |
---|
Links: |
---|
Umfang: |
6 |
---|
doi: |
10.1063/1.351053 |
---|
funding: |
|
---|---|
Förderinstitution / Projekttitel: |
|
PPN (Katalog-ID): |
NLEJ218619995 |
---|
LEADER | 01000caa a22002652 4500 | ||
---|---|---|---|
001 | NLEJ218619995 | ||
003 | DE-627 | ||
005 | 20230506004709.0 | ||
007 | cr uuu---uuuuu | ||
008 | 081125s1992 xx |||||o 00| ||eng c | ||
024 | 7 | |a 10.1063/1.351053 |2 doi | |
035 | |a (DE-627)NLEJ218619995 | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
245 | 1 | 0 | |a Synthesis and crystal growth of the high-Tc phase in Bi–Pb–Sr–Ca–Cu–O system with variation of excess concentrations of CaO and CuO |
264 | 1 | |c 1992 | |
300 | |a 6 | ||
336 | |a nicht spezifiziert |b zzz |2 rdacontent | ||
337 | |a nicht spezifiziert |b z |2 rdamedia | ||
338 | |a nicht spezifiziert |b zu |2 rdacarrier | ||
520 | |a Analyzing the results measured by x-ray powder diffraction, scanning electron microscope, energy dispersion x-ray analysis, and the standard four-probe techniques for eight groups of samples with different compositions of excess CaO and CuO, after quenching and annealing, shows that not only the much more stable 2223 phase in the Bi(Pb)–Sr–Ca–Cu–O system was obtained in a high fraction, but also its grain (plate shaped) size could be made larger than normally sintered. We attribute these effects to the annealing and/or the excess contents of CaO and CuO selected in this study. | ||
533 | |f AIP Digital Archive | ||
650 | 4 | |a HIGH−TC SUPERCONDUCTORS | |
650 | 4 | |a BISMUTH OXIDES | |
650 | 4 | |a LEAD OXIDES | |
650 | 4 | |a STRONTIUM OXIDES | |
650 | 4 | |a CALCIUM OXIDES | |
650 | 4 | |a COPPER OXIDES | |
650 | 4 | |a SYNTHESIS | |
650 | 4 | |a CRYSTAL GROWTH | |
650 | 4 | |a CHEMICAL COMPOSITION | |
650 | 4 | |a PHASE STUDIES | |
650 | 4 | |a X−RAY DIFFRACTION | |
650 | 4 | |a SCANNING ELECTRON MICROSCOPY | |
700 | 1 | |a Wu, Qianzhang |4 oth | |
700 | 1 | |a Fu, Zhengmin |4 oth | |
700 | 1 | |a Zhang, Aizhen |4 oth | |
700 | 1 | |a Huang, Jiashan |4 oth | |
700 | 1 | |a Tang, Disheng |4 oth | |
700 | 1 | |a Yao, Pei |4 oth | |
700 | 1 | |a Chu, Shaoyan |4 oth | |
700 | 1 | |a Yi, Sunsheng |4 oth | |
700 | 1 | |a Rong, Xishen |4 oth | |
700 | 1 | |a Zhang, Anzhi |4 oth | |
700 | 1 | |a Cheng, Xianan |4 oth | |
773 | 0 | 8 | |i In |t Journal of Applied Physics |d [S.l.], 1931 |g 71(1992), 6, Seite 2772-2777 |h Online-Ressource |w (DE-627)NLEJ217994199 |w (DE-600)1476463-5 |x 1089-7550 |7 nnns |
773 | 1 | 8 | |g volume:71 |g year:1992 |g number:6 |g pages:2772-2777 |g extent:6 |
856 | 4 | 0 | |u http://dx.doi.org/10.1063/1.351053 |
912 | |a GBV_USEFLAG_U | ||
912 | |a ZDB-1-AIP | ||
912 | |a GBV_NL_ARTICLE | ||
936 | s | n | |a U |2 EZB |
951 | |a AR | ||
952 | |d 71 |j 1992 |e 6 |h 2772-2777 |g 6 |