Development and Characterization of Lightweight Geopolymer Composite Reinforced with Hybrid Carbon and Steel Fibers
The aim of this paper is to analyze the influence of hybrid fiber reinforcement on the properties of a lightweight fly ash-based geopolymer. The matrix includes the ratio of fly ash and microspheres at 1:1. Carbon and steel fibers have been chosen due to their high mechanical properties as reinforcement. Short steel fibers (SFs) and/or carbon fibers (CFs) were used as reinforcement in the following proportions: 2.0% wt. CFs, 1.5% wt. CFs and 0.5% wt. SFs, 1.0% wt. CFs and 1.0% wt. SFs, 0.5% wt. CFs and 1.5% wt. SFs and 2.0% wt. SFs. Hybrid reinforcement of geopolymer composites was used to obtain optimal strength properties, i.e., compressive strength due to steel fiber and bending strength due to carbon fibers. Additionally, reference samples consisting of the geopolymer matrix material itself. After the production of geopolymer composites, their density was examined, and the structure (using scanning electron microscopy) and mechanical properties (i.e., bending and compressive strength) in relation to the type and amount of reinforcement. In addition, to determine the thermal insulation properties of the geopolymer matrix, its thermal conductivity coefficient was determined. The results show that the addition of fiber improved compressive and bending strength. The best compressive strength is obtained for a steel fiber-reinforced composite (2.0% wt.). The best bending strength is obtained for the hybrid reinforced composite: 1.5% wt. CFs and 0.5% wt. SFs. The geopolymer composite is characterized by low thermal conductivity (0.18-0.22 W/m ∙ K) at low density (0.89-0.93 g/cm3).
Medienart: |
E-Artikel |
---|
Erscheinungsjahr: |
2021 |
---|---|
Erschienen: |
2021 |
Enthalten in: |
Zur Gesamtaufnahme - volume:14 |
---|---|
Enthalten in: |
Materials (Basel, Switzerland) - 14(2021), 19 vom: 01. Okt. |
Sprache: |
Englisch |
---|
Beteiligte Personen: |
Baziak, Agnieszka [VerfasserIn] |
---|
Links: |
---|
Themen: |
Carbon fiber |
---|
Anmerkungen: |
Date Revised 16.10.2021 published: Electronic Citation Status PubMed-not-MEDLINE |
---|
doi: |
10.3390/ma14195741 |
---|
funding: |
|
---|---|
Förderinstitution / Projekttitel: |
|
PPN (Katalog-ID): |
NLM331809435 |
---|
LEADER | 01000naa a22002652 4500 | ||
---|---|---|---|
001 | NLM331809435 | ||
003 | DE-627 | ||
005 | 20231225214300.0 | ||
007 | cr uuu---uuuuu | ||
008 | 231225s2021 xx |||||o 00| ||eng c | ||
024 | 7 | |a 10.3390/ma14195741 |2 doi | |
028 | 5 | 2 | |a pubmed24n1105.xml |
035 | |a (DE-627)NLM331809435 | ||
035 | |a (NLM)34640137 | ||
035 | |a (PII)5741 | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
100 | 1 | |a Baziak, Agnieszka |e verfasserin |4 aut | |
245 | 1 | 0 | |a Development and Characterization of Lightweight Geopolymer Composite Reinforced with Hybrid Carbon and Steel Fibers |
264 | 1 | |c 2021 | |
336 | |a Text |b txt |2 rdacontent | ||
337 | |a ƒaComputermedien |b c |2 rdamedia | ||
338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
500 | |a Date Revised 16.10.2021 | ||
500 | |a published: Electronic | ||
500 | |a Citation Status PubMed-not-MEDLINE | ||
520 | |a The aim of this paper is to analyze the influence of hybrid fiber reinforcement on the properties of a lightweight fly ash-based geopolymer. The matrix includes the ratio of fly ash and microspheres at 1:1. Carbon and steel fibers have been chosen due to their high mechanical properties as reinforcement. Short steel fibers (SFs) and/or carbon fibers (CFs) were used as reinforcement in the following proportions: 2.0% wt. CFs, 1.5% wt. CFs and 0.5% wt. SFs, 1.0% wt. CFs and 1.0% wt. SFs, 0.5% wt. CFs and 1.5% wt. SFs and 2.0% wt. SFs. Hybrid reinforcement of geopolymer composites was used to obtain optimal strength properties, i.e., compressive strength due to steel fiber and bending strength due to carbon fibers. Additionally, reference samples consisting of the geopolymer matrix material itself. After the production of geopolymer composites, their density was examined, and the structure (using scanning electron microscopy) and mechanical properties (i.e., bending and compressive strength) in relation to the type and amount of reinforcement. In addition, to determine the thermal insulation properties of the geopolymer matrix, its thermal conductivity coefficient was determined. The results show that the addition of fiber improved compressive and bending strength. The best compressive strength is obtained for a steel fiber-reinforced composite (2.0% wt.). The best bending strength is obtained for the hybrid reinforced composite: 1.5% wt. CFs and 0.5% wt. SFs. The geopolymer composite is characterized by low thermal conductivity (0.18-0.22 W/m ∙ K) at low density (0.89-0.93 g/cm3) | ||
650 | 4 | |a Journal Article | |
650 | 4 | |a carbon fiber | |
650 | 4 | |a cenosphere | |
650 | 4 | |a geopolymer composite | |
650 | 4 | |a hybrid reinforcement | |
650 | 4 | |a lightweight composite | |
650 | 4 | |a microsphere | |
650 | 4 | |a steel fiber | |
700 | 1 | |a Pławecka, Kinga |e verfasserin |4 aut | |
700 | 1 | |a Hager, Izabela |e verfasserin |4 aut | |
700 | 1 | |a Castel, Arnaud |e verfasserin |4 aut | |
700 | 1 | |a Korniejenko, Kinga |e verfasserin |4 aut | |
773 | 0 | 8 | |i Enthalten in |t Materials (Basel, Switzerland) |d 2009 |g 14(2021), 19 vom: 01. Okt. |w (DE-627)NLM208535349 |x 1996-1944 |7 nnns |
773 | 1 | 8 | |g volume:14 |g year:2021 |g number:19 |g day:01 |g month:10 |
856 | 4 | 0 | |u http://dx.doi.org/10.3390/ma14195741 |3 Volltext |
912 | |a GBV_USEFLAG_A | ||
912 | |a GBV_NLM | ||
951 | |a AR | ||
952 | |d 14 |j 2021 |e 19 |b 01 |c 10 |