Influence of composition and powder/water ratio on adhesion strength and initial viscosity of powder-type denture adhesives based on CMC-Na and PVM-MA
We evaluated the influence of the composition and powder/water (P/W) ratio of powder-type denture adhesives (DA) based on sodium carboxymethyl cellulose (CMC-Na) and poly(methyl vinyl ether-maleic anhydride) (PVM-MA) on the strength of adhesion to acrylic resin and initial viscosity. Twenty types of DA were prepared by mixing CMC-Na and PVM-MA at various weight ratios with distilled water in P/W ratios ranging from 0.125 to 0.500. Adhesion strength and viscosity were measured using a universal testing machine and a controlled-stress rheometer, respectively. A higher percentage of CMC-Na and higher P/W ratios resulted in higher adhesion strength and viscosity. The effect of the CMC-Na/PVM-MA weight ratio on adhesion strength and viscosity was larger than that of the P/W ratio. DA with higher viscosity had higher adhesion strength. These results suggest that the adhesion strength and initial viscosity of powder-type DA can be controlled via the P/W ratio and the CMC-Na/PVM-MA weight ratio.
Medienart: |
E-Artikel |
---|
Erscheinungsjahr: |
2019 |
---|---|
Erschienen: |
2019 |
Enthalten in: |
Zur Gesamtaufnahme - volume:38 |
---|---|
Enthalten in: |
Dental materials journal - 38(2019), 6 vom: 01. Dez., Seite 994-1001 |
Sprache: |
Englisch |
---|
Beteiligte Personen: |
Okazaki, Hitomi [VerfasserIn] |
---|
Links: |
---|
Themen: |
059QF0KO0R |
---|
Anmerkungen: |
Date Completed 03.12.2019 Date Revised 03.12.2019 published: Print-Electronic Citation Status MEDLINE |
---|
doi: |
10.4012/dmj.2018-307 |
---|
funding: |
|
---|---|
Förderinstitution / Projekttitel: |
|
PPN (Katalog-ID): |
NLM30120103X |
---|
LEADER | 01000naa a22002652 4500 | ||
---|---|---|---|
001 | NLM30120103X | ||
003 | DE-627 | ||
005 | 20231225104132.0 | ||
007 | cr uuu---uuuuu | ||
008 | 231225s2019 xx |||||o 00| ||eng c | ||
024 | 7 | |a 10.4012/dmj.2018-307 |2 doi | |
028 | 5 | 2 | |a pubmed24n1003.xml |
035 | |a (DE-627)NLM30120103X | ||
035 | |a (NLM)31511472 | ||
040 | |a DE-627 |b ger |c DE-627 |e rakwb | ||
041 | |a eng | ||
100 | 1 | |a Okazaki, Hitomi |e verfasserin |4 aut | |
245 | 1 | 0 | |a Influence of composition and powder/water ratio on adhesion strength and initial viscosity of powder-type denture adhesives based on CMC-Na and PVM-MA |
264 | 1 | |c 2019 | |
336 | |a Text |b txt |2 rdacontent | ||
337 | |a ƒaComputermedien |b c |2 rdamedia | ||
338 | |a ƒa Online-Ressource |b cr |2 rdacarrier | ||
500 | |a Date Completed 03.12.2019 | ||
500 | |a Date Revised 03.12.2019 | ||
500 | |a published: Print-Electronic | ||
500 | |a Citation Status MEDLINE | ||
520 | |a We evaluated the influence of the composition and powder/water (P/W) ratio of powder-type denture adhesives (DA) based on sodium carboxymethyl cellulose (CMC-Na) and poly(methyl vinyl ether-maleic anhydride) (PVM-MA) on the strength of adhesion to acrylic resin and initial viscosity. Twenty types of DA were prepared by mixing CMC-Na and PVM-MA at various weight ratios with distilled water in P/W ratios ranging from 0.125 to 0.500. Adhesion strength and viscosity were measured using a universal testing machine and a controlled-stress rheometer, respectively. A higher percentage of CMC-Na and higher P/W ratios resulted in higher adhesion strength and viscosity. The effect of the CMC-Na/PVM-MA weight ratio on adhesion strength and viscosity was larger than that of the P/W ratio. DA with higher viscosity had higher adhesion strength. These results suggest that the adhesion strength and initial viscosity of powder-type DA can be controlled via the P/W ratio and the CMC-Na/PVM-MA weight ratio | ||
650 | 4 | |a Journal Article | |
650 | 4 | |a Adhesion strength | |
650 | 4 | |a CMC-Na | |
650 | 4 | |a Denture adhesive | |
650 | 4 | |a PVM-MA | |
650 | 4 | |a Viscosity | |
650 | 7 | |a Adhesives |2 NLM | |
650 | 7 | |a Dental Cements |2 NLM | |
650 | 7 | |a Water |2 NLM | |
650 | 7 | |a 059QF0KO0R |2 NLM | |
650 | 7 | |a Sodium |2 NLM | |
650 | 7 | |a 9NEZ333N27 |2 NLM | |
700 | 1 | |a Yoshida, Kazuhiro |e verfasserin |4 aut | |
700 | 1 | |a Egoshi, Takafumi |e verfasserin |4 aut | |
700 | 1 | |a Takase, Kazuma |e verfasserin |4 aut | |
700 | 1 | |a Murata, Hiroshi |e verfasserin |4 aut | |
773 | 0 | 8 | |i Enthalten in |t Dental materials journal |d 1985 |g 38(2019), 6 vom: 01. Dez., Seite 994-1001 |w (DE-627)NLM012859230 |x 1881-1361 |7 nnns |
773 | 1 | 8 | |g volume:38 |g year:2019 |g number:6 |g day:01 |g month:12 |g pages:994-1001 |
856 | 4 | 0 | |u http://dx.doi.org/10.4012/dmj.2018-307 |3 Volltext |
912 | |a GBV_USEFLAG_A | ||
912 | |a GBV_NLM | ||
951 | |a AR | ||
952 | |d 38 |j 2019 |e 6 |b 01 |c 12 |h 994-1001 |